【摘 要】
：
The effects of the annealing process on the mechanical properties and crystallization behaviors of polypropylene random copolymer (PP-R) composites were investigated using differential scanning calorimetry (DSC), wide-angle X-ray diffraction (WAXD), and d
【机 构】
：
College of Materials and Architectural Engineering, Guizhou Normal University, Guiyang 550025, China
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The effects of the annealing process on the mechanical properties and crystallization behaviors of polypropylene random copolymer (PP-R) composites were investigated using differential scanning calorimetry (DSC), wide-angle X-ray diffraction (WAXD), and dynamic mechanical analysis (DMA), and scanning electron microscopy (SEM). The experimental results indicated that the annealing process significantly influenced the comprehensive properties of PP-R composites. At temperatures below 23 ℃, the impact strength of the PP-R composites annealed at 120 ℃ for 6 h was relatively high at 74.73 k J/m2, which was 16.8％ higher than that of the samples annealed at 80 ℃ for 6 h. At low temperatures (-30-0 ℃), the impact strength ranged from approximately 13.31 k J/m2 to 54.4 k J/m2. In addition, the annealing process conducted at 120 ℃ for 6 h improved the crystalline structure and low-temperature toughness of the PP-R composites and induced α-form to β-form crystal transformation. The work provides a possible method to reinforce and toughen the semicrystalline polymer at low temperatures (-30-0 ℃) by annealing.
其他文献
Nano hafnium carbide (HfC) powders were synthesized by sol-gel combining hightemperature rapid heat treatment process using citric acid and hafnium tetrachloride as the raw materials. The effects of ball milling treatment on the phase and morphology of py
Three-dimensionally ordered (3DOM) macroporous phosphotungstic acid/SiO2 (HPW/SiO2) materials were prepared by using colloidal crystal as templates and applied for oxidative desulfurization (ODS) of the model fuel oil. The obtained HPW/SiO2 materials were
To understand the enhancing effect and fiber-reinforced mechanism of composite fibers reinforced cement concrete, the influences of composite fibers on micro-cracks and the distribution of composite fibers were evaluated by optical electron micrometer (OE
The parameters for the electro-deposition of Cu were optimized in order to increase the compressive properties of close cell aluminum. Different values of deposition voltages and times were considered to vary the amount of deposited Cu. The surface morpho
A simple and fast method of preparation of vanadium carbide (V8C7) nanopowders using mechanical alloying assisted microwave heating method was demonstrated. The micron-sized V2O5 and nano-sized carbon black were used as starting materials. The as-prepared
The effects of aging time and temperature on the formation and growth behavior of interfacial intermetallic compound (IMC) of Sn-16Sb/Cu(wt％) solder joints prepared by using dip soldering were investigated. The results show that the major IMCs between Sn-
Titania (TiO2) nanorod powder was prepared by nonhydrolytic sol-gel method using titanic chloride (TiCl4) as titanium source, methylene dichloride (CH2Cl2) as solvent, absolute ethyl alcohol (CH-3CH2OH) as oxygen donor. The effects of Si4+ doping on the T
Ce-doped Bi2O3 nanopowders were prepared by reverse titration chemical coprecipitation from Bi3+ and Ce 4+ containing aqueous solution.Techniques of X-ray diffraction(XRD),transmission electron microscopic(TEM)and Fourier transform infrared spectroscopy(F
A fixed-point observation method was designed to research the dynamic tribologieal performance of one certain resin-based friction materials.The friction test was performed through a constant speed friction tester under various temperature conditions.It w
Polydimethylsiloxane (PDMS)-polystyrene (PS) interpenetrating polymer network (IPN) was prepared and characterized by FTIR, TGA, WCA, swelling experiments, and SEM. The IPN was used for pervaporation (PV) recovery of butanol. Both the permeation flux and