【摘 要】
：
研究了低合金高强钢加热过程奥氏体晶粒长大规律和合金元素的固溶规律。结果表明,随着保温时间延长,奥氏体平均晶粒尺寸逐渐增大。加热到1200℃时,未溶相主要为NbC、TiC;均热
【机 构】
：
辽宁科技大学材料与冶金学院,钢铁研究总院特殊钢研究所,
论文部分内容阅读
研究了低合金高强钢加热过程奥氏体晶粒长大规律和合金元素的固溶规律。结果表明,随着保温时间延长,奥氏体平均晶粒尺寸逐渐增大。加热到1200℃时,未溶相主要为NbC、TiC;均热时间为10 min时,Ti、Nb固溶达到平衡,固溶率分别为92.4%和13.6%。实验室条件下,适宜加热温度选定在1150~1200℃之间,保温时间约10 min。
The rules of austenite grain growth and the solution of alloying elements in low-alloy high-strength steel during heating were studied. The results show that the average grain size of austenite gradually increases with the holding time prolonging. When heated to 1200 ℃, the undissolved phase is mainly NbC and TiC. When the soaking time is 10 min, the solid solution of Ti and Nb reaches equilibrium, and the solid solution rate is 92.4% and 13.6% respectively. Under laboratory conditions, suitable heating temperature is selected between 1150 ~ 1200 ℃, holding time is about 10 min.
其他文献
随着新时代的发展,建筑行业也在发生日新月异的变化,一些传统的以二维表现的施工方案已经无法满足使用需求.本文通过对BIM技术的应用在通过虚拟施工将这两点结合,对施工方案
教育不断的开展进步,关于培养学生体育素质这方面越来越为人所重视,近年来伴随我国具体相关教育体制的深入改革,高职院校体育教学已然不再维持过往仅仅简单停留保持于学生体
2013年3月20日,克里夫兰速贷球馆。勒布朗·詹姆斯在一场NBA常规赛中得到了27分,和以往一样,全场掀起了山呼海啸的呐喊声,但如果你仔细听,就会发现这并不是鼓舞助威,而是嘘声
自治区第十一次党代会以来,在自治区党委、政府的坚强领导下,银川市委、市政府团结带领全市人民,加快推进开放内涵式发展,干在实处、走在前列,全市经济保持稳步快速增长。经
Al-Zn-Mg合金在长时间的时效中存在双峰硬化现象,为了模拟析出硬化动力学,基于改进的Langer–Schwartz方法发展了不同析出物形成的双峰硬化模型。该物理模型考虑了Al-Zn-Mg合
01我国完成加纳微堆低浓化项目准备工作,进入现场实施阶段5月27日上午,由中核集团承担的加纳微堆低浓化项目国内准备工作均已完成,低浓铀燃料正式启运。这标志着加纳微堆低浓
“按规定,我们要有暂住证,可我们夫妻俩在这边打工没办过;还要提供在家没有监护条件的证明,回家办过一趟,很麻烦。——最后,在京打工的边琴琴把女儿留在了农村。有调查显示,
岭澳核电站大修时多次出现卸压模式下一回路排水过程中水位计RCP090/098MN指示偏差过大,导致一回路排水被迫停止,延误了大修关键路径的情况。本文就RCP090/098MN出现偏差的原
随着社会的发展,经济形式的改变,蕴涵着藏民族精神的藏族传统体育文化正在悄无声息的淡出主流体育文化。本文通过文献资料法、访谈法等对社会变迁下藏族传统体育文化存在的问
11月8日至12日,以“金贵之州,绿色运动,放飞梦想”为主题的黔西南州第三届运动会在兴义举行,近2000多名运动员齐聚一堂,全面展示该州体育成果。尽管比赛当天阴雨绵绵,但是参