【摘 要】
：
采用共沉淀法合成镧掺杂氧化铈的前驱体,经高温煅烧后得到纳米镧掺杂氧化铈粉体,对所得产物进行了TG-DSC、XRD、FE-SEM、HR-TEM及XPS一系列表征。结果表明,两步法制备的镧掺
【机 构】
：
北京科技大学,中国科学院过程工程研究所多相复杂系统国家重点实验室,
论文部分内容阅读
采用共沉淀法合成镧掺杂氧化铈的前驱体,经高温煅烧后得到纳米镧掺杂氧化铈粉体,对所得产物进行了TG-DSC、XRD、FE-SEM、HR-TEM及XPS一系列表征。结果表明,两步法制备的镧掺杂氧化铈是由平均尺寸为2～8nm的纳米晶粒组成的花状微米球。镧最大掺杂量可达70%,且产物仍能保持氧化铈的立方萤石结构。大比例镧掺杂可以在氧化铈晶体中产生大量的晶体缺陷及氧空位。
The precursors of lanthanum-doped ceria were synthesized by co-precipitation method. After lanthanum-doped ceria powders were calcined at high temperature, the products were characterized by TG-DSC, XRD, FE-SEM, HR-TEM and XPS Characterization. The results show that the two-step lanthanum-doped ceria is a flower-shaped microsphere composed of nanocrystalline grains with an average size of 2-8 nm. Lanthanum maximum doping up to 70%, and the product can still maintain the cubic fluorite structure of cerium oxide. Large proportion of lanthanum doping can produce a large number of crystal defects and oxygen vacancies in the cerium oxide crystal.
其他文献
HDH(氢化脱氢)钛粉末颗粒形状不规则、流动性较差,不利于注射成形和提高其制品性能.本研究利用PCS系统对HDH钛粉末颗粒进行整形,考察了处理工艺,用扫描电镜和粒度分析表征处
为了向洁净钢冶炼提供一种无碳的精炼钢包渣线用材料,将MgO/Si_3N_4复合耐火材料应用于精炼钢包渣线是一项有意义的探索.借助SEM和EDAX等手段研究了MgO/ Si_3N_4复合材料在精
为提升我国重庆市高职院校篮球的教学效率,对篮球这项运动进行更进一步的推广,以重庆市高职院校篮球教学的现状为基础,分析了我国重庆市高职院校篮球改革的背景与指导思想,并
准确的知道关于企业运营和财务情况,在如今市场压力剧烈的市场和现代化体系渐渐改良的竞争中,对于企业经营者和外部权益者都是至关重要的,若要做出明确的选择和判定,都应当对
利用XRD、SEM和电阻应变片等方法研究了Tb0.3Dy0.7(Fe1-xPtx)1.95(x=0.00,0.02,0.04,0.06,0.08)合金的微结构和磁致伸缩特性。结果表明:当Pt含量x≤0.06时,合金为具有立方MgC
随着新时期的到来,我国社会主义现代化建设步入了新的发展阶段,党在十八大上对我国工会工作进行了明确部署,并提出了新的任务与要求。因此,如何提升工会干部的综合素质已经成
随着我国改革开放的深入和各项事业的快速发展，习主席在十八大会议中明确指出，在新的历史条件和历史背景下，我国社会上还有一股力量，那就是要充分发挥和调动这些离退休老干部在实
对8mm高功率二次谐波回旋速调放大器进行了理论研究和优化设计,已研制出回旋速调放大器实验样管,并进行了热测实验,得到了如下结果:在中心频率为35GHz的情况下,得到的最大脉
当前,随着我国油田企业的不断改革与发展,要求油田思想政治工作要紧跟时代发展步伐,在新形势下健康前行,全面推广与宣传油田思想政治工作的优势,以推动油田整体发展为根本目
针对建筑企业施工现场管理存在如现场管理理念落后、项目管理体系不健全等问题,进行原因分析,在此基础上,将“6S”现场管理方法,应用在建筑企业现场管理中,对增强其综合竞争