A chemically robust superhydrophobic nanocomposite thin film with enhanced wear resistance is prepared from a composite comprising polytetrafluoroethylene(PTFE) and carbon nanotubes.The superhydrophobic thin films with hierarchical structure are fabricated by spraying an environmentally friendly aqueous dispersion containing carbon nanotubes and PTFE resin on silicon wafer.Thin films with a contact angle of 154.1°± 2° and a sliding angle less than 2° remain superhydrophobic after abrading over 500 times under a pressure of 50 g/cm~2.The thin film is also extremely stable even under much stress conditions.To further the understanding of the enhancement of wear resistance,we investigated the formation of microsized structure and their effects.The growth of microbumps is caused by attracting solution droplet to the hydrophilic islands on hydrophobic surface.
A chemically robust superhydrophobic nanocomposite thin film with enhanced wear resistance is prepared from a composite comprising polytetrafluoroethylene (PTFE) and carbon nanotubes. Superhydrophobic thin films with hierarchical structure are fabricated by spraying an environmentally friendly aqueous dispersion containing carbon nanotubes and PTFE resin on silicon wafer .Thin films with a contact angle of 154.1 ° ± 2 ° and a sliding angle less than 2 ° remain superhydrophobic after abrading over 500 times under a pressure of 50 g / cm ~ 2. The thin film is also extremely stable even under much stress conditions. further in understanding the enhancement of wear resistance, we investigated the formation of microsized structure and their effects. growth of microbumps is caused by attracting solution droplet to the hydrophilic islands on hydrophobic surface.