The aim of this study was to improve the cyclic oxidation resistance of In718 superalloy by laser peening(LP). Specimens were treated by LP from one to three times, respectively. The cyclic oxidation tests at 900℃ for periods up to 2 h were conducted. Cha
【机 构】
：
School of Mechanical Engineering, Jiangsu University, Zhenjiang 212013, China;School of Material Sci
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The aim of this study was to improve the cyclic oxidation resistance of In718 superalloy by laser peening(LP). Specimens were treated by LP from one to three times, respectively. The cyclic oxidation tests at 900℃ for periods up to 2 h were conducted. Changes of the top surface morphology and microstructure were analyzed by scanning electron microscope (SEM), energy-dispersive spectra (EDS), transmission electron microscope (TEM) and X-ray diffraction technique (XRD), respectively. The weights were measured between the oxidation cycles to assess the oxidation of the specimens. The top surface microstructure after LP was characterized by highly tangled and dense dislocation arrangements and a high amount of twins. Protective oxidation layer was generated more quickly on the surface treated by LP. The average oxidation rate was about 50 % lower. A tiny homogeneous oxidation layer containing (Fe,Cr)2O3, NiCrO3 and Ni(Al,Cr)2O4 spinel was generated on the surface. The experimental results of cyclic oxidation tests show that specimens treated by LP have a better high temperature oxidation resistance, and the antistrip performance of the oxidation layer improves. Moreover, the effects of LP are strengthened with the increase of laser peening.
其他文献
The correlation between the microhardness and microstructure features of anodic films on 2024 aluminum alloy formed in the mixed sulfuric acid/oxalic acid electrolyte was studied using micro-hardness tester and scanning electron microscope (SEM). The resu
Recent achievements in concrete hydration exothermic models based on Arrhenius equation have improved computation accuracy for mass concrete temperature field. But the properties of the activation energy and the gas constant (Ea/R) have not been well stud
The combined microarc oxidation (MAO) and magnetron sputtering deposition process was used to deposit duplex a-C:H/MAO and Ti-a-C:H/MAO coatings on AM80 magnesium alloy. The microstructure, mechanical properties and tribological behavior of the two duplex
The starch-g-lactic acid copolymer was synthesized with catalysis of sulfuric acid by one-step process, and the structure of starch-g-lactic acid copolymer was characterized by means of IR, 13C-NMR, HMBC, XRD, and SEM. The experimental results show that t
Fe-based amorphous and nanocrystalline coatings were fabricated by air plasma spraying. The coatings were further treated by laser remelting process to improve their microstructure and properties. The corrosion resistance of the as-sprayed and laser-remel