【摘 要】
：
对RPC材料的局部抗压性能进行研究。通过对39块RPC试块的局部抗压试验,确定RPC材料延性破坏的局压面积比应控制在Ab/Al
【机 构】
：
北京城建五维市政工程有限公司,中铁第五勘察设计院集团有限公司,北京铁路局天津工务段,
论文部分内容阅读
对RPC材料的局部抗压性能进行研究。通过对39块RPC试块的局部抗压试验,确定RPC材料延性破坏的局压面积比应控制在Ab/Al<10;得出RPC的局部抗压开裂及极限强度提高系数分别为cβr=0.57016(Ab/Al)0.67135,β=0.9(Ab/Al)1/2。对有预应力孔道的RPC试块的局部抗压强度进行研究,并与预应力钢筋的预拉应力进行比较,最终确定RPC预应力结构锚下无需间接配筋。
The local compressive properties of RPC materials were studied. Through the local compressive tests of 39 RPC test blocks, the area ratio of the partial pressure of the ductile damage of the RPC material should be controlled at Ab / Al <10; the coefficient of increase of local compressive cracking and ultimate strength of RPC is cβr = 0.57016 (Ab / Al) 0.67135, β = 0.9 (Ab / Al) 1/2. The local compressive strength of RPC specimens with prestressed tunnels was studied and compared with the prestressing stress of prestressing steel bars. Finally, no indirect reinforcement under RPC prestressed structure anchors was determined.
其他文献
以乙醇为溶剂,以超声波作为提取辅助设备,通过单因子试验确定影响黄酮化合物提取的主要因素及其最佳水平范围,通过L9(34)正交试验确定其最优提取条件,研究超声波辅助提取九香
研究了液体环氧树脂精制工艺中加碱方式和用量,助催化剂种类及用量以及反应时间等对产品质量的影响,得到了最优精制工艺:第1次NaOH用量为粗树脂中有机氯物质的量,反应时间0.5
惊情90秒扑朔迷离的谍影,惊天动地的爆破,狂飙突进的飞车,007式的英雄与美人,万人追逐的明星加上一个意想不到的结局……原本一部90分钟的好莱坞大片剧情,被浓缩在短短的90秒
目的建立测定银杏叶中总内酯含量的一测多评的方法。方法以白果内酯为指标,建立银杏内酯A、银杏内酯B、银杏内酯C与白果内酯之间的相对校正因子,以样品中测出的白果内酯含量
制备了固体酸催化剂Zr(SO4)2蛐TiO2,并将其用于合成马来酸二丁酯,考察了Zr(SO4)2与TiO2的质量比、焙烧温度、焙烧时间等催化剂制备条件对催化活性的影响.采用FTIR与DTG对催化
介绍了形状记忆合金(shape memory alloy,简称SMA)的主要特性,建立了SMA阻尼器的热力学平衡方程,并通过实验分析了SMA阻尼参数对结构风振控制效果的影响,结果表明:在相同屈服
随着我国改革开放的不断深入,宾馆成为第三产业在近几年得到迅猛发展。继市场经济体制逐步确立后,旅游饭店、宾馆的经营逐渐进入竞争市场。宾馆业已从宾馆的硬件建设转到加
通过介绍燃气企业在经营过程中形成供销差的各种原因以及控制供销差的方法,说明供销差管理对燃气企业的重要性。
By introducing various reasons why the gas business for
目的通过分析恩施州2011年手足口病病原体检测结果,了解该病在恩施州的流行特征,为制订预防控制策略提供依据。方法采集恩施州各县(市)报告手足口病患者咽拭子、疱疹液、肛拭
目的:观察莪术醇对人结直肠癌Lo Vo细胞裸鼠移植瘤的抑制作用,探讨其可能的机制。方法:建立人结直肠癌Lo Vo细胞裸鼠移植瘤模型,成瘤后将其随机分为莪术醇高、中、低剂量(80,