Shape-stablized EP/Paraffin Composite for Latent Heat Storage
【机 构】
：
College of Materials Science and Engineering, Nanjing University of Technology, Nanjing 210009, Chin
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
【发表日期】
：
2013年4期
其他文献
Nanoindentation Mechanical Properties and Structural Biomimetic Models of Three Species of Insects W
Mimicking insect flights were used to design and develop new engineering materials. Although extensive research was done to study various aspects of lfying insects. Because the detailed mechanics and underlying principles involved in insect lfights remain
Enhancing Heterogeneous Catalytic Activity of Iron (II) Phthalocyanine by Ethanol and Its Applicatio
A chemical system for facile and accurate detection of 2,4-dichlorophenol (DCP) via iron (II) phthalocyanine (Fe(II)Pc) catalyzed chromogenic reaction is reported for the first time. In this system, DCP could be oxidized by dioxygen with the catalysis of
Porosity and Pore Size Distribution Measurement of Cement/Carbon Nanofiber Composites by Low Field N
The aim of this study was to improve the capacity for crack-repair in concrete by developing a new way. The self-healing agent based on biological carbonate precipitation was developed. Crack-healing capacity of the cement paste specimens with this bioche
Effect of Fast Cooling Rate on the Microstructure and Mechanical Properties of Low-Carbon High-Stren
The effect of fast cooling rate on the microstructure and mechanical properties of low-carbon high-strength steel annealed in the intercritical region was investigated using a Gleeble 1500 thermomechanical simulator and a continuous annealing thermomechan
Influence of Superplasticizers on Early Age Drying Shrinkage of Cement Paste with the Same Consisten
The influence of superplasticizer (SP) on the early age drying shrinkage of cement paste with the same consistency was investigated. To conduct the test, which lasted for 72 hours, three paste mixtures were used for comparison. The 72 hours early age dryi
Poly(vinyl alcohol)/collagen (PVA/COL) micro-nanofibers were successfully prepared by electrospinning process. Water, green, and non-toxic was used as the solvent. The electrospun mats consisted of micro-nanoscale ifbers with mean diameter ranging from ap
GeS6 chalcogenide amorphous film was deposited on glass substrate via PLD (pulsed laser deposition) technique. The performance and structure of the film was characterized by XRD (X-ray diffraction), SEM (Scanning Electron Microscopy), EDS (Energy Dispersi