【摘 要】
：
Based on the ABAQUS / Explicit finite element method, the forming force changing trend of deep drawing test for 6A16 aluminum alloy plate after pre-aging and storage at room temperature for one month was simulated under friction coefficient ranging from 0
【机 构】
：
State Key Laboratory of Nonferrous Metals and Processes, GRIMAT Engineering Institute Co., Ltd., Bei
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Based on the ABAQUS / Explicit finite element method, the forming force changing trend of deep drawing test for 6A16 aluminum alloy plate after pre-aging and storage at room temperature for one month was simulated under friction coefficient ranging from 0 to 0.22. The lubricants selected for the tests were mechanical oil, butter and dry film lubricant, and the friction coefficient of these lubricants were 0.05, 0.10 and 0.15, respectively. Microstructural evolution of 6A16 aluminum alloy plate during drawing forming was investigated by OM, SEM and EBSD. The results showed that, with the increase of friction coefficient, the stress, strain and deformation degree in deformation zone increased, while the grain size in deformation zone decreased. Thus, the hardness of the cup-typed component increased with the increase of friction coefficient. Butter-lubricated cups had the highest tensile strength and yield strength after paint-bake cycle. The combination of simulation results and microstructure analysis of 6A16 aluminum alloy plate after drawing forming indicates that the appropriate lubricant is butter.
其他文献
In the absence of commonly used seed layer, we can still successfully synthesized aligned ZnO nanowire arrays by the hydrothermal method. By using aluminum-doped zinc oxide (AZO) glass as a substrate, high-density and vertically aligned ZnO nanowires were
LDHs was introduced into 70# asphalt binder by different weight ratio. Asphalt penetration test, soft point test, ductility test, viscosity test, dynamic shear rheometer (DSR) test and Fourier transform infrared (FTIR) test, were conducted to characterize
Slag glass melting is usually performed on a laboratory scale in crucibles, which are economically viable tools for the production of slag glass-ceramics. In this work, quaternary CaO-Al2O3-MgO-SiO2 (CAMS) glass-ceramics were prepared by melting the taili
The microstructural evolution of C-(A)-S-H gel in Portland cement pastes immersed in pure water and 5.0 wt％ Na2SO4 solution for different ages was comparatively investigated, by means of 29Si NMR spectroscopy, and SEM-EDS analysis. Additionally, molecular
Ferroelectric and leakage properties are important for ferroelectric applications. Pure and Nd-doped (x=0.05-0.20) BiFeO3 thin films were fabricated by sol-gel method on FTO substrates. The phase structure, surface morphology, leakage current, ferroelectr
Amphiphilic CS-SA polymers were prepared using the SA modified by small molecule water-soluble chitosan, and CS-SA nanomicelles and FF/CS-SA nanomicelles were prepared by using CSSA polymers as the material with dialysis-ultrasound method. CS-SA polymers,
A modified Bridgman directional solidification technique was used to prepare Fe-Al-Ta eutectic in situ composites at different growth rates ranging from 6 to 80 μm/s. The directionally solidified Fe-Al-Ta eutectic composites are composed of two phases: Fe
Early hydration mechanism of cement-based materials with silica fume, nano-SiO2 and silica sol of different contents was investigated, and the detailed effect of these Si-rich mineral admixtures in three stages of early hydration (NG, I, D) using kinetics
In order to fabricate a novel ZnO/cotton composite, a high proportion of ZnO nanoparticles were assembled in cotton fibers, and the as-obtained cotton fabric can possess better UV blocking property compared with common ZnO/cotton composite. Firstly, the c
The preparation of hydroxyl chromium oxide by hydrogen reduction of disodium chromate and particulate hydroxyl mechanical activation features were studied. Then with self-made hydroxyl chromium as the raw material, a direct reduction and carburization pro