Mechanical properties of a Gum-type Ti–Nb–Zr–Fe–O alloy

来源 :International Journal of Minerals Metallurgy and Materials | 被引量 : 0次 | 上传用户:ie_down
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
A new Gum-type alloy(Ti–Nb–Zr–Fe–O) in which Fe is used instead of Ta was subjected to a particular thermomechanical processing scheme to assess whether its mechanical characteristics(fine ?-grains with high strength and low modulus) render it suitable as a biomedical implant material. After a homogenization treatment followed by cold-rolling with 50% reduction, the specimens were subjected to one of three different recrystallization treatments at 1073, 1173, and 1273 K. The structural and mechanical properties of all of the treated specimens were analyzed. The mechanical characterization included tensile tests, microhardness determinations, and fractography by scanning electron microscopy. The possible deformation mechanisms were discussed using the Bo – Md diagram. By correlating all of the experimental results, we concluded that the most promising processing variant corresponds to recrystallization at 1073 K, which can provide suitable mechanical characteristics for this type of alloys: high yield and ultimate tensile strengths(1038 and 1083 MPa, respectively), a low modulus of elasticity(62 GPa), and fine crystalline grain size(approximately 50 ?m). A new Gum-type alloy (Ti-Nb-Zr-Fe-O) in which Fe is used instead of Ta was subjected to a particular thermomechanical processing scheme to assess whether its mechanical characteristics (fine -grains with high strength and low modulus After a homogenization treatment followed by cold-rolling with 50% reduction, the specimens were subjected to one of three different recrystallization treatments at 1073, 1173, and 1273 K. The structural and mechanical properties of The mechanical characterization includes tensile tests, microhardness determinations, and fractography by scanning electron microscopy. By may corrective all of the experimental results, we concluded that the most promising processing variant corresponds to recrystallization at 1073 K, which can provide suitable mechanical characteristics for this t ype of alloys: high yield and ultimate tensile strengths (1038 and 1083 MPa, respectively), a low modulus of elasticity (62 GPa), and fine crystalline grain size (approximately 50 μm).
其他文献
诺如病毒是导致人类急性胃肠炎的主要食源性致病原,由于变异快且缺乏稳健的体外细胞培养体系及小动物感染模型,限制了我们对该病原体的深入研究.近年来,可培养鼠源诺如病毒的
Good news came from the energy field 3 years after President Xi Jinping proposed the Belt and Road Initiative and right as the one-month countdown to the first
透明质酸酶是能降解透明质酸及部分糖胺聚糖的一类糖苷酶,可应用于医疗和美容等领域.透明质酸酶也可用于制备小分子糖胺寡糖,许多研究发现小分子糖胺寡糖具有比大分子糖胺聚
何海霞大师关门弟子中国极具影响力的山水画名家赵道珍赵道珍,男,1952年生,现居北京,笔名走峭,艺名蒙山居士、峭幽斋主。1997被美术教育家、国画大师何海霞先生收为关门弟子,
目的:探讨体外致敏成熟树突状细胞(DC)与细胞因子诱导杀伤细胞(CIK)共培养细胞群对人舌鳞癌细胞系Tca8113移植瘤裸鼠的体内抑瘤效果。方法:人舌鳞癌外周血分离培养DC,体外诱