Wettability of molten Sn-Ag-Cu alloy on Cu substrate has been determined by sessile drop method, as well as its dependence on time and temperature. It was found that the evolution of contact angle at the alloy’s melting point experienced four different stages. Especially, the contact angle was unstable and fluctuant in stage II, and gradually decreased in stage III mainly due to a chemical reaction between Sn-Ag-Cu alloy and Cu substrate. The contact angle decreased with increasing temperature, but increased slightly at 629 K, for another chemical reaction occurred. Interfacial characteristic has been further investigated by examining the sample’s cross section. Intermetallic compounds of Cu6Sn5 and β-Sn phase were found at the interface of Sn-Ag-Cu/Cu. Wettability of molten Sn-Ag-Cu alloy on Cu substrate has been determined by sessile drop method, as well as its dependence on time and temperature. It was found that the evolution of contact angle at the alloy’s melting point experienced four different stages. Especially , the contact angle was unstable and fluctuant in stage II, and gradually decreased in stage III mainly due to a chemical reaction between Sn-Ag-Cu alloy and Cu substrate. The contact angle decreased with increasing temperature, but increased slightly at 629 K, For another chemical reaction occurred. Interfacial characteristic has been further investigated by examining the sample’s cross section. Intermetallic compounds of Cu6Sn5 and β-Sn phase were found at the interface of Sn-Ag-Cu / Cu.