具有优良耐磨减摩性能的铝表面润滑性功能膜的研制和开发越来越受到重视,并己开始应用。目前,国内对这种膜的工艺及性能尚研究较少,为探讨这种功能膜实际应用的可能,对该膜的综合性能进行了检测和评定。一、试验方法暴露面积为14×50mm的工业纯铝片状样品经清洗、电解抛光后,于15%(wt)硫酸中,9℃,2.7A/dm~2直流电下阳极氧化制得硬质膜。然后在10%HNO_3中活化10分钟,再置于0.5%(Wt)的硫代钼酸胺溶液中,以100mA/dm~2的直流电进行二次阳极
More and more attention has been paid to the development and development of the functional lubricated aluminum film with excellent abrasion and friction reducing properties and its application has started. At present, the domestic technology and performance of this film is still less studied, in order to explore the practical application of this functional film possible, the film’s overall performance testing and assessment. First, the test method The exposed area of 14 × 50mm industrial pure aluminum flake samples after cleaning, electrolytic polishing, in 15% (wt) sulfuric acid, 9 ℃, 2.7A / dm ~ 2 DC current anodized hard membrane. Then activated in 10% HNO3 for 10 minutes and placed in a 0.5% (Wt) thiomolybdate solution at a secondary current of 100 mA / dm2