In this study,alumina/A380 composite coatings were fabricated by cold spray.The influence of alumina particulates\' morphology (spherical and irregular) and content on the deposition behavior of the coatings (including surface roughness,surface residual
【机 构】
：
Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China;School of Materials
论文部分内容阅读
In this study,alumina/A380 composite coatings were fabricated by cold spray.The influence of alumina particulates\' morphology (spherical and irregular) and content on the deposition behavior of the coatings (including surface roughness,surface residual stress,cross-sectional microstructure and microhardness) was investigated.Results revealed that the spherical alumina mainly shows micro-tamping effect during deposition,which result in remarkable low surface roughness and porosity of the coatings.In addition,very low deposition efficiency and good interfacial bonding between the coating and the substrate were achieved.For irregular alumina particles,the embedding of ceramic particulates in the coating was dominant during deposition process,resulting in high retention in the final deposit.However,it showed limited influence on porosity,surface roughness and interfacial bonding of the deposit.The coatings containing irregular alumina particulates exhibited much higher microhardness than those containing spherical alumina due to the higher load-bearing capacity of deposited alumina.
其他文献
The corrosion evolution processes of steel reinforced concrete under simulated tidal and immersion zones of marine environment were investigated by using electrochemical measurements and corrosion morphology observations.The results indicate that the corr
The correlation between particle in-flight parameter,defect content and mechanical property of yttria-stabilized zirconia coating was systematically studied in the present work.The melting state of in-flight particle during spraying was simulated using co
The high-strain-rate mechanical response of Mg alloy/SiCp composite foams has received increased attention in recent years due to their light weight and potential to absorb large amounts of energy during deformation.Dynamic compressive properties of close
To study the effects of the deformation degree and cooling rate on the microstructure and phase transformation temperature for the B1500HS steel,the samples were heated at 900 ℃ for 5 min,compressed by 10,20,30 and 40％ at the strain rate of 0.1 s-1,and th
Effect of aging heat treatment on the grain boundary microstructure and creep properties of a cast Ni-based superalloy was investigated.With increasing aging temperature from 750 to 1000 ℃,M23C6 carbides along the grain boundaries evolve from fine distrib
The effect of simulated acidified marine aerosols on the corrosion morphology of carbon steel was studied using an in situ optical stereomicroscope and scanning electron microscope equipped with an energy-dispersive spectrometer and a white-light interfer
Cerium malate (CeMal) was tested as a corrosion inhibitor for AA2024-T3 in this work.Corrosion inhibition on bare AA2024-T3 indicated that the inhibiting effect was a result of the synergistic effect of cerium cations and maleic anions.The corrosion of AA
Pre-alloyed powder of Ti2AlNb alloy was prepared by electrode induction gas atomization method,and the powder was screened into five kinds of powder size distribution.Fully dense Ti2AlNb alloy was prepared by powder metallurgy (PM) using hot isostatic pre
The recycling of high Fe-content Al-Si alloys is a green industry.Eliminating the harmful effect of Fe,achieving the separation of A1 and Fe is one of the key problems.Different from traditional methods for iron removal,a novel method using magnesium melt
β-Nb is a typical second phase in Zr-Nb-based alloys used as fuel claddings in water-cooled nuclear reactors.The segregation of alloying element Fe may affect the corrosion resistance of Zr-Nb-based alloys.In this work,the Fe segregation at the interface