【摘 要】
：
The effect of reactive element yttrium on purification and carbide precipitation of superalloy K4169 has been studied through vacuum induction melting.The results show that yttrium has a strong deoxidizing and desulfurizing ability,and the impurity elemen
【机 构】
：
Shi-Changxu Innovation Center for Advanced Materials,Institute of Metal Research,Chinese Academy of
论文部分内容阅读
The effect of reactive element yttrium on purification and carbide precipitation of superalloy K4169 has been studied through vacuum induction melting.The results show that yttrium has a strong deoxidizing and desulfurizing ability,and the impurity elements of sulfur and oxygen in melting K4169 are greatly reduced to 2-5 ppm and 4-5 ppm,respectively.The metallurgical reaction product is mainly Y2O3 and yttrium containing sulfides have not been observed.With the increase of the content of yttrium from 0.005 wt.％to 0.033 wt.％,the morphology and size of MC carbides in casting are significantly influenced due to that the yttrium changes the diffusion of the carbide forming elements and solid fraction during solidification.In the alloys without yttrium,only isolated blocky or strip carbides exist,while skeleton-like carbides are observed in the alloys with yttrium.Both the average size and the number density of skeleton carbides decrease monotonously with yttrium content increasing.After yttrium increasing to 0.033 wt.％,a phase of hexagonal Ni17Y2 is observed to precipitate in the form of symbiosis with MC carbide and matrix.The addition of yttrium is not beneficial for the properties of K4169 alloys at the room temperature,which is quite related to the MC carbides with a large skeleton-like morphology through the analysis of tensile fracture.
其他文献
Temperature-responsive resistance transition behaviors of the melamine sponges wrapped with different graphene oxide derivatives(i.e.nanoribbon,wide-ribbon and sheet)were investigated.Melamine sponge composites coated by three types of GO derivatives were
Heterogeneous Pd nanocatalysts are efficient catalysts for the Heck reaction but require multi-step,sophisticated procedures and harsh reaction conditions.In this work,a green and facile strategy has been developed to decorate Pd nanoparticles on polydopa
Tilt probe penetrating friction stir welding(PFSW)was an innovative technology proposed in recent years to avoid the formation of kissing bond in the root of joint.However,with the heat input decreasing,“S”line or zigzag line was easily introduced in the
This work investigates the strain rate dependence of dynamic recrystallization behaviour of high-purity zinc in room temperature compression under strain rates of 10-4 s-1,10-2 s-1 and 0.5 s-1.Results from electron backscatter diffraction provide insight
Aging treatment of Cu-based alloys is essential to enhance their strength that is desirable for their exten-sive engineering applications in electrical industry,whereas the underlying mechanism of strengthening is essential for massive manufacturing of th
A valid strategy to tailor the properties of polylactic acid for more extensive applications was introducing filler.In this work,basalt fiber assembled with in-situ SiO2 nanoparticles on the surface was successfully prepared via hydrothermal method and it
Laser 3D printing based on melt growth has great potential in rapid preparation of Al2O3-based eutectic ceramics.In this work,large-scale Al2O3/GdAlO3/ZrO2 ternary eutectic ceramic rod with diameter of 4-5 mm and height higher than 250 mm was additively m
Many metal matrix self-lubricating composites possess excellent comprehensive properties of high strength and wear resistance after incorporating various lubricants that usually belong to ceramic phase.However,this improvement is always obtained at the co
Radial forging(RF)is an economical manufacturing forging process,in which four dies arranged radially around the workpiece simultaneously act on the workpiece with high-frequency radial movement.In this study,a ZK60 magnesium alloy step-shaft bar was proc
Grain-boundary(GB)precipitation has a significant adverse effect on plasticity of alloys,which easily leads to catastrophic intergranular failure in safety-critical applications under high external loading.Herein,we report a novel strategy that uses the l