【摘 要】
：
本文用失重法和慢应变率法确定16Mn钢在3％氯化钠水溶液中适宜阴极保护电位区间,用扫描电镜观察慢应变拉伸断口形貌。结果表明:16Mn钢在3％氯化钠水溶液中适宜阴极保护电位区间是
【机 构】
：
南京化工学院应用化学系,南京化工学院应用化学系,南京化工学院应用化学系,
论文部分内容阅读
本文用失重法和慢应变率法确定16Mn钢在3％氯化钠水溶液中适宜阴极保护电位区间,用扫描电镜观察慢应变拉伸断口形貌。结果表明:16Mn钢在3％氯化钠水溶液中适宜阴极保护电位区间是:-775mVSCE——-900mVSCE。阴极过保护电位下,16Mn钢将发生以沿晶脆断为特征的氢脆,而且保护电位越负,其氢脆敏感性越大。
In this paper, 16Mn steel was determined to be cathodic protection potential in 3% aqueous solution of sodium chloride by weight loss method and slow strain rate method. The morphology of slow strain tensile fracture was observed by scanning electron microscope. The results show that the optimum cathodic protection potential of 16Mn steel in 3% sodium chloride aqueous solution is -775mVSCE --- 900mVSCE. Cathode over the protective potential, 16Mn steel will occur along the brittle fracture along the characteristics of hydrogen embrittlement, and the more protective potential, the greater the sensitivity of hydrogen embrittlement.
其他文献
对MgO-B_2O_3-MgCl_2-H_2O浓盐溶液结晶析出氯柱硼镁石(2MgO·2B_2O_3·MgCl_2·14H_2O)的动力学过程进行了研究。利用单纯形优化法配合Runge-Kutta微分方程组数值解法对实验
1.带预紧力的滚珠丝杠传动装置(苏联发明证书号1120136)可用于数控机床进给传动装置和机器人中。预紧力的调整过程如下:拧出螺钉1(图1),并借助支顶螺钉6,取下盖5。在螺母4端
冷轧取向硅钢片高温加热时,二次晶粒形核于极表面附近的区域,核的长大方式与冷轧形变率有关。本文按二次冷轧工艺、H1-B(一次冷轧)工艺下二次晶核的长大特点,分别采用能量分
采用失重法,极化曲线法和 SEM 研究了硫酸盐还原菌(SRB)诱导碳钢腐蚀的主要因素。实验结果表明,在 SRB 的代谢过程中,会产生一种挥发性的含磷化合物,它具有一定的腐蚀性,但导
前言投资数十亿巨款建成的高压造型工厂到处都存在着问题,然而这些问题并非采用高压造型后才出现的,早在70～71年以后新建的中压造型工厂中,绝大部分都是有问题的,并经常发生
我们生产的金属零件,加工完毕后都要去毛刺,常用的方法有:手工去毛刺、车床去毛刺、滚桶去毛刺、化学去毛刺、爆炸去毛刺、高压去毛刺等。而一些薄壁、细长、精度要求较高的
<正> 本文谈的是巴巴拉·麦克林托克——一位科学家,一位被她的同事认为是自行其事和忱于幻想的人,同一门科学——遗传学——这两者怎样相互影响的故事。遗传学在最近数十年
近年来,哲学界对耗散结构理论及化学振荡的研究非常感兴趣,许多哲学书和杂志都从哲学的角度发表了各自的见解,仅《化学哲学基础》一书就有两篇文章专论此课题。当然,由于这
目的比较不同宣传方式在口腔科医院感染控制中的效果。方法选取326例口腔手术患者随机分为对照组和观察组,对照组患者予以常规健康宣教,观察组患者采用针对性的健康宣教方式
为探讨二脱氧肌苷(ddI)对培养的背根神经节(DRG)神经元的影响,我们对分散培养的胎鼠DRG神经元培养3d后,再分别以不同浓度的ddI(1μg/ml,5μg/ml,10μg/mll和20μg/ml)孵育3d