【摘 要】
：
采用原位聚合法制备了PA11(尼龙11)/GO(GO)纳米复合材料,并采用XLY-Ⅱ型毛细管流变仪研究了共混物的流变特性。结果表明:PA11及其复合材料均为假塑性流体,呈现切力变稀的现象
【机 构】
：
中北大学材料科学与工程学院,常州大学材料科学与工程学院,
论文部分内容阅读
采用原位聚合法制备了PA11(尼龙11)/GO(GO)纳米复合材料,并采用XLY-Ⅱ型毛细管流变仪研究了共混物的流变特性。结果表明:PA11及其复合材料均为假塑性流体,呈现切力变稀的现象;非牛顿指数n均小于1。随着GO含量的增加,PA11/GO纳米复合材料的表观黏度升高,粘流活化能下降,表明共混材料的表观黏度对温度的敏感性降低,易于加工成型。
PA11 (nylon 11) / GO (GO) nanocomposites were prepared by in-situ polymerization. The rheological properties of the blends were investigated by X-R-II capillary rheometer. The results show that both PA11 and its composites are pseudoplastic fluids, showing the phenomena of shear thinning; the non - Newtonian index n is less than 1. With the increase of GO content, the apparent viscosity of PA11 / GO nanocomposites increased, and the activation energy of viscous flow decreased. It indicated that the apparent viscosity of blends decreased the sensitivity to temperature and was easy to process and shape.
其他文献
目的 探讨人性化护理在哮喘患者中的应用效果.方法 将100例哮喘患者以人性化护理为分界点分为观察组和对照组,对照组采用常规护理,观察组在对照组的基础上采用人性化护理,比
肱骨近端骨折是指肱骨外科颈在内及其以上部位的骨折,是临床上常见骨折之一.据相关文献报道其发生率在4％～5％[1],往往累及肱骨近端骨骺[2].骨折端的血供、骨折类型、骨质情况对于
胎儿生长受限(fetal growth restriction,FGR)是指胎儿出生体质量低于同孕龄胎儿平均体质量的2个标准差,或低于同龄正常体质量胎儿的第10百分位数.FGR不仅直接影响胎儿及新生
糖尿病血管钙化、动脉粥样硬化是诱发心、脑血管疾病的原因之一[1].动脉粥样斑块形成是导致心血管疾病最常见的病理改变,但近年对糖尿病血管并发症的研究发现,除动脉粥样斑块
呼吸道合胞病毒(RSV)是严重危害婴幼儿和小儿健康最常见的下呼吸道感染病原体.有报道表明,RSV所引起的小儿急性下呼吸道感染的病例占所有小儿下呼吸道感染病例的70％[1].其高危
过敏性肺炎(hypersensitivity pneumonitis,HP)是一组由不同致敏原引起的非哮喘性变应性肺部疾病,以弥漫性间质炎为其病理特征.由于吸入含有真菌孢子、细菌产物、动物蛋白质
目的 分析盆底肌肉功能锻炼治疗女性轻中度压力性尿失禁(SUI)的临床疗效.方法 收集中轻度SUI女性患者102例,随机分为观察组与对照组各51例,对照组实施常规产后健康教育,观察
目的 研究乳腺导管扩张症的临床特点及临床治疗的方法.方法 选取我院收治的24例乳腺导管扩张症的患者作为研究对象,观察该疾病的临床特点及外科手术治疗的效果.结果 乳腺导管
针对宣钢两条链箅机-回转窑氧化球团生产线存在设计缺陷,设备故障率高,生产不能连续稳定,严重制约产量的问题,通过实施一系列改造和生产调整,收到了良好效果,保证了设备正常
采用X射线衍射和电化学方法,研究了正极材料Li3 Ni0.1V19(PO4)3的结构和电化学性能.结果表明:Li3 Ni0.1V1.9(PO4)3具有单斜晶系结构.在室温下,以0.1C倍率放电时Li3Ni0.1V1.9(