The A1NP/2024 composite with a high volume fraction (50%) was fabricated by squeeze casting. Its mechanical properties were investigated by tensile tests at ambient temperature and the microstructure was observed by a transmission electron microscope (TEM ). It was indicated that after six thermal cooling cycles treatment the AIN/2024Al composite exhibited higher elastic limit (ac.ol), tensile strength (UTS) and elastic modulus (E). TEM observation showed that there was higher dislocation density both in the matrix and the particle. hi phase is the mainly precipitate.
The A1NP / 2024 composite with a high volume fraction (50%) was fabricated by squeeze casting. Its mechanical properties were investigated by tensile tests at ambient temperature and the microstructure was observed by a transmission electron microscope (TEM). It was indicated that after six thermal cooling cycles treatment the AIN / 2024Al composite bearing higher elastic limit (ac.ol), tensile strength (UTS) and elastic modulus (E). TEM observation showed that there was higher dislocation density both in the matrix and the particle. hi phase is the mainly precipitate.