【摘 要】
：
为改善粉煤灰的表面活性,用硅烷偶联剂KH-560对粉煤灰表面进行改性,采用X射线衍射、红外光谱、透射电子扫描电镜等对改性前后的粉煤灰进行表征。研究结果表明:KH-560能够在粉
【机 构】
：
石家庄铁道大学材料科学与工程学院,河北省交通工程材料重点实验室,
论文部分内容阅读
为改善粉煤灰的表面活性,用硅烷偶联剂KH-560对粉煤灰表面进行改性,采用X射线衍射、红外光谱、透射电子扫描电镜等对改性前后的粉煤灰进行表征。研究结果表明:KH-560能够在粉煤灰表面产生很好的化学键合,包覆在粒子表面,阻止颗粒的团聚,从而使改性粉煤灰均匀分散在聚氨酯弹性体中,与基体形成物理和化学交联结构。
In order to improve the surface activity of fly ash, the surface of fly ash was modified with silane coupling agent KH-560, and the fly ash before and after modification was characterized by X-ray diffraction, infrared spectroscopy and transmission electron microscopy. The results show that: KH-560 can produce good chemical bonding on the surface of fly ash, coated on the particle surface to prevent the agglomeration of particles, so that the modified fly ash is evenly dispersed in the polyurethane elastomer, forming physical And chemical cross-linked structure.
其他文献
以煤萃取反萃取法分离所得煤密中质组分溶胶为涂覆液,通过添加聚乙二醇和氯化锌两种改性剂,研究了它们对制备的陶瓷-炭复合膜性能的影响,考察了复合膜的孔隙率、纯水渗透率以
高温固相法制备正极材料Li1.1(Ni1/3Co1/3Mn1/3)1-xCrxO2-yFy,用X射线衍射仪(XRD)和扫描电子显微镜(SEM)对材料的结构和形貌进行表征,用恒电流充放电测试系统测试材料的电化
德国rn研发多种替代功能材料,在燃料电池催化剂方面获得突破.rn替代材料方面:弗劳恩霍夫陶瓷技术和烧结材料研究所应用冻干—直接发泡法开发出一种新型的烃基磷灰石/氧化锆复
以硝酸锌、六亚甲基四胺为原料,通过低温水浴方法在芳纶Ⅲ表面实现氧化锌纳米棒的修饰。采用X射线衍射仪、扫描电子显微镜、能量色散X射线谱仪、紫外分光光度计和热失重仪等
钯(Pd)作为燃料电池阳极催化剂,具有重要的市场应用前景。从纯Pd催化剂,负载型Pd催化剂,Pd基合金催化剂3个方面综述了近年来Pd催化剂在燃料电池阳极中的研究进展,介绍了其结
以六氯环三磷腈为原料,合成了六(4-炔丙基苯氧基)环三磷腈(PPT),并将其与PET共混制备PET/PPT混合材料.通过红外光谱(FT-IR)和核磁共振(1 H-NMR、31 P-NMR)表征了PPT结构.利用
以苯肼和对甲氧基肉桂酸甲酯等为原料,合成了一种重金属离子捕集剂1-苯基-5-(4-甲氧基苯基)-3-羟基吡唑铜(DPHP).研究了DPHP用量、pH、搅拌时间、温度对含氯化锰模拟废水溶液
研究了多壁碳纳米管水分散体系的紫外光谱特征及其影响因素,并将其应用于碳纳米管对环境污染物五氯苯酚的吸附过程。结果表明:水分散多壁碳纳米管的主吸收带在190~250nm;最大
以农业废料中的油菜秸秆为原料,利用化学活化的方法制备活性炭。利用活性炭对甲基橙的吸附探讨了料液比、活化剂磷酸浓度、活化时间、活化温度、浸泡时间对活性炭吸附能力的
合成了一系列烯丙基修饰的咪唑类离子液体,使用FT-IR和1H-NMR对产物结构进行表征.在常温、常压下,对合成的离子液体进行分离CO2性能研究.结果表明,烯丙基修饰的咪唑类离子液