The electrical properties of solder contact layers between Cu-Ni shunt metal and tube type Bi2212 superconductor that is applied in superconducting fault current limiter were studied.The contact properties of the solders are improved not only by Ag precoating layers,but also by the pre-sprayed Ag layer and subsequent Ag precoating layers.The annealed Ag sprayed layers onto Bi2212 superconductor prior to Ag electroplating work as protecting layers for the superconductor from plating solutions.The contact angle of the electroplated Ag layer is 42.91° and decreases to 15.25° and 5.88° with Ag sprayed layer and additional Ag electroplated layers.The Ag sprayed layer with suitable annealing prior to Ag electroplating improves contact strength of the Ag electroplated layer by about 12% due to denser microstructure of the Ag electroplated layers.
The electrical properties of solder contact layers between Cu-Ni shunt metal and tube type Bi2212 superconductor that is applied in superconducting fault current limiter were studied. The contact properties of the solders are improved not only by Ag precoating layers, but also by the pre- sprayed Ag layer and subsequent Ag precoating layers. The annealed Ag sprayed layers onto Bi2212 superconductor prior to Ag electroplating work as protecting layers for the superconductor from plating solutions. The contact angle of the electroplated Ag layer is 42.91 ° and decreases to 15.25 ° and 5.88 ° with Ag sprayed layer and additional Ag electroplated layers. The Ag sprayed layer with the appropriate annealing prior to Ag electroplating improves contact strength of the Ag electroplated layer by about 12% due to denser microstructure of the Ag electroplated layers.