Regimes of continuous and pulsed laser action on high-melting oxide compounds of ZrO2 were found with the aim of obtaining steady coatings on monocrystal silicon on laser ablation.X-ray phase analyses,scanning and atomic-force microscopy reveal that the coatings obtained are of nanocluster structure with the cubic ordering.In this case the nanoclusters reach several hundreds of nanometers in size.An assumption was made that on laser ablation of ZrO2 thermostabilization may take place where a minimum of the surface energy is attained just at cubic ordering.
Regimes of continuous and pulsed laser action on high-melting oxide compounds of ZrO2 were found with the aim of obtaining steady coatings on monocrystal silicon on laser ablation. X- ray phase analyzes, scanning and atomic-force microscopy reveal the coatings obtained are nanocluster structure with the cubic ordering. In this case the nanoclusters reach several hundreds of nanometers in size. An assumption was made that on laser ablation of ZrO2 thermostabilization may take place where a minimum of the surface energy is attained just at cubic ordering.