The microstructure and magnetic properties of cobalt ferrite thin films deposited by the sputtering method on an Fe3O4 under-layer were investigated at different post-annealing temperatures.Results show that the Fe3O4 under-layer can accelerate the grain growth of cobalt ferrite films due to the phase transformation of the Fe3O4 under-layer at about 400°C-500°C.By introducing the Fe3O4 under-layer,cobalt ferrite nanocrystalline thin films with high coercivity can be obtained at lower post-annealing temperatures.
The microstructure and magnetic properties of cobalt ferrite thin films deposited by the sputtering method on an Fe3O4 under-layer were investigated at different post-annealing temperatures. Results show that the Fe3O4 under-layer can accelerate the grain growth of cobalt ferrite films due to the phase transformation of the Fe3O4 under-layer at about 400 ° C-500 ° C.By introducing the Fe3O4 under-layer, cobalt ferrite nanocrystalline thin films with high coercivity can be obtained at lower post-annealing temperatures.