用等离子向不锈钢丝上沉积铝的方法,生产了铝基纤维强化试样,把含有大量氧化物的特别不均匀的铝表面层压成了均匀的基体。通过压制就消除了表征原始表面的半连续氧化膜的残痕,该原始表面类似于压制光滑铝叠层板时所见到的那种表面。断口金相照片表明,等离子沉积和热压工艺使纤维与基体之间产生了良好的焊合。 Using plasma to deposit aluminum onto a stainless steel wire, an aluminum-fiber-reinforced test specimen was produced, which laminated a particularly non-uniform aluminum surface containing a large amount of oxide into a uniform matrix. The residue characterizing the semicontinuous oxide film of the original surface is eliminated by pressing, which is similar to the kind of surface seen when compressing a smooth aluminum laminate. Fracture metallographic photographs show that the plasma deposition and hot pressing process produces a good weld between the fiber and the substrate.