【摘 要】
：
Mechanical properties and microstructures of AE42 magnesium alloy with addition of Zn and subjected to hot extrusion at 370 ℃ and an extrusion ratio of 8-1 wer
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
Mechanical properties and microstructures of AE42 magnesium alloy with addition of Zn and subjected to hot extrusion at 370 ℃ and an extrusion ratio of 8-1 were investigated. The results show that for the AE42 alloy, the addition of Zn can obviously improve its elongation as well as the ultimate tensile and yield strengths below 150 ℃. The addition of Zn can refine the microstructure of the AE42 alloy, and result in the precipitation of Mg17Al12 and MgZn2 phases. Due to the addition of Zn to the AE42 alloy, the amount of Al11RE3 phase decreases, while the Al11RE3 phase becomes short rod-shaped from acicular and block, and distributes along the grain boundaries, which will have a stronger effect on the tensile properties of the alloy at elevated temperature. In addition, with the presence of MgZn2 precipitates, the sliding of grain boundaries is restrained and the strength of the alloy gets enhanced.
其他文献
A series of experimental studies were conducted on the recrystallization of directionally solidified cobalt-base superalloy DZ40M. It is found that the secondar
The structure characteristic and electric performance of ZnO film deposited on nucleation side of free-standing diamond substrates under different heating tempe
If the reverse transformation of a shape memory alloy is arrested, a kinetic stop will appear in the next complete transformation. The kinetic stop temperature
The electroless nickel plated graphite fibers reinforced aluminum matrix composites (Gr(Ni)/Al) were produced by squeeze casting, and the microstructure of Gr(N
The production of 2,3-butanediol by Klebsiella pneumoniae from glucose supplemented with different salts was studied. A suitable medium composition was defined
YBa2Cu4O8/La2/3Ca1/3MnO3/YBa2Cu4O8 (Y-124/LCMO/Y-124) heterostructure was prepared by facing-target sputtering technique. The oscillatory superconducting transi
The effects of didymium(Nd:Pr=3:1)on the microstructure and mechanical properties of Mg-10%Al alloy were studied with the additions of 0～3%Di. The small block-li
Nanophosphor with the nominal composition of Ca0.8Zn0.2TiO3∶Pr3+, Na+ (CZTOPN) was synthesized at relatively low temperature by the sol-gel method. Metal ions
Strontium doped lanthanum manganite (LSM) powders were synthesized by three different routes: azeotropic distillation, sol-gel and solid state reaction respecti
The technique of solution deposition was employed to prepare Li4Ti5O12 thin film using lithium acetate and TiO(C4H9)4 as starting materials. The structural and