Microstructures and mechanical properties of Nd: YAG laser welded transformation induced plasticity (TRIP) steel with tensile strength of 645 MPa were studied. Due to high cooling speed of laser welding, the weld metal mainly consists of martensite different from the base metal, which is composed of ferrite matrix with bainite and a little retained austenite. Therefore, the weld metal has maximum hardness at welded joint. The yield strength and tensile strength of welded specimens tested perpendicular to weld line were almost equal to those of the base metal. But the yield strength and tensile strength of welded specimens tested parallel with weld line were a little higher than those of the base metal. The formability of laser welded TRIP steel was decreased compared with that of the base metal.