【摘 要】
：
Thin films of hydrazine molybdenum (MoO4N4H6), a new inorganic azo dye, were synthesized and deposited on a commercial glass substrate using the chemical bath d
【机 构】
：
Department of Science Education
论文部分内容阅读
Thin films of hydrazine molybdenum (MoO4N4H6), a new inorganic azo dye, were synthesized and deposited on a commercial glass substrate using the chemical bath deposition technique. Subsequently, the optical transmission, reflectivity, absorption, refractive index, and dielectric constant of hydrazine molybdenum were investigated using an ultraviolet-visible spectrophotometer. In addition, the film structure was analyzed by mid-infrared spectroscopy. The spectra of the films were found to be in line with those in the literature. The sur-face properties of all films were examined using a computer-controlled digital scanning electron microscope with a secondary electron de-tector. The areas of application and the technological advantages of this material were also considered.
其他文献
目的:探讨攀爬运动中四肢双关节肌的功能现象。方法:任选上海体育学院20名男生,抗自重、不限定姿势进行三种向上攀爬(爬绳、爬竿、引体向上)的运动实验。采用运动解剖学动作
在阿哌沙班的结构基础上,保持其P1部分不变,对其P4部分进行结构改造,用一系列芳香酰胺基团代替2-氮己酮,合成了一系列未见报道的吡唑并吡啶酮类化合物.所合成化合物结构均经I
Tempering is an important process for T/P92 ferritic heat-resistant steel from the viewpoint of microstructure control, as it facili-tates the formation of fina
The hot deformation behaviors of GH4706 alloy were investigated using compression tests in a deformation temperature range from 900°C to 1200°C with a strain
For strip steel with the thickness of 1.6 mm,the yield and tensile strengths as high as 760 and 850 MPa,respectively,were achieved using the compact strip produ
Composite briquettes containing high-phosphorus oolitic hematite and coal were produced with a twin-roller briquette machine using sodium carboxymethyl cellulos
We have systematically studied the microstructure and mechanical properties of Ni-5wt%Al and Ni-20wt%Al composite coat-ings fabricated on 6061-T6 aluminum alloy
Ti-Mo alloys with various Mo contents from 6wt%to 14wt%were processed by spark plasma sintering based on elemental pow-ders. The influence of sintering temperat
(Mg66.2Zn28.8Ca5)100-xCux (at%, x=0, 1, 3, and 5) bulk metallic glasses (BMGs) of 2 mm in diameter were prepared by the con-ventional copper mold injection cast
This study proposes an efficient way to utilize all the chemical components of the basic oxygen furnace(BOF) slag to prepare high value-added glass-ceramics.A m