The resistance of the anodic PbO film fonned on lead at 0.9 V (vs. Hg/Hg2SO4) in 4.5 mol/dm3 H2SO4 was measured using alternating-current impedance method. The resistance of the anodic PbO film was found to be close to that of the interstitial liquid among the PbO particles in the film, suggesting that the interstitial liquid may serve as the major passage for ion transportation during the film growth.
The resistance of the anodic PbO film fonned on lead at 0.9 V (vs. Hg / Hg2SO4) in 4.5 mol / dm3 H2SO4 was measured using alternating-current impedance method. The resistance of the anodic PbO film was found to be close to that of the interstitial liquid among the PbO particles in the film, suggesting that the interstitial liquid may serve as the major passage for ion transportation during the film growth.