A preparation technology of MgO powder used in special silicon steel from hydromagnesite mineral has been developed. The preparation technology includes the following steps: (1) calcining the hydromagnesite at 700-750°C for 1.5-2 h; (2) hydrating the calcined hydromagnesite to be slurry containing the solid-liquid ratio of 15-20 g?L?1; (3) acquiring Mg(HCO3)2 solution by carbonating the slurry, the carbonation temperature, CO2 pressure, and end point PH value of carbonation are less than 40°C, 0.4-0.6 MPa, and 7 respectively during the carbonation process; (4) preparing precipitated basic magnesium carbonate by thermally decomposing the Mg(HCO3)2 solution at 90-100°C; (5) obtaining the MgO product by calcining the precipitated basic magnesium carbonate at 850-950°C for 30-60 min, and adopting flowing nitrogen during the cooling process. By using this technology, more than 80wt% magnesium in hydromagnesite mineral can be extracted, and high-performance MgO products used in special silicon steel can be ob- tained.
A preparation technology of MgO powder used in special silicon steel from hydromagnesite mineral has been developed. The preparation technology includes the following steps: (1) calcining the hydromagnesite at 700-750 ° C for 1.5-2 h; (2) hydrating the calcined (3) 获得 Mg (HCO3) 2 solution by carbonating the slurry, the carbonation temperature, CO2 pressure, and end point PH value of carbonation are hydromagnesite to be slurry containing solid-liquid ratio of 15-20 g? L? less than 40 ° C, 0.4-0.6 MPa, and 7 respectively during the carbonation process; (4) preparing precipitated basic magnesium carbonate by be decomposed the Mg (HCO3) 2 solution at 90-100 ° C; product by calcining the precipitated basic magnesium carbonate at 850-950 ° C for 30-60 min, and through flowing nitrogen during the cooling process. By using this technology, more than 80 wt% magnesium in hydromagnesite mineral can be extracted, and high-performance MgO products used in special s ilicon steel can be ob- tained.