【摘 要】
：
Experiments were carried out to investigate the corrosion behavior of epoxy-coated rebar (ECR) with pinhole defect (diameter in hundreds of microns) immersed in the uncarbonated/carbonated simulated pore solution (SPS) of seawater concrete.Corrosion behav
【机 构】
：
School of Materials Science and Engineering, University of Science and Technology of China, Hefei 23
论文部分内容阅读
Experiments were carried out to investigate the corrosion behavior of epoxy-coated rebar (ECR) with pinhole defect (diameter in hundreds of microns) immersed in the uncarbonated/carbonated simulated pore solution (SPS) of seawater concrete.Corrosion behavior was analyzed by electrochemical impedance spectroscopy.The composition and morphology of corrosion products were characterized by X-ray diffraction,energy-dispersive spectrometry and scanning electron microscopy.Meanwhile,oxide film produced by preheating before spray coating was investigated by X-ray photoelectron spectroscopy and Mott-Schottky technology.Results indicated that corrosion behavior of ECR with pinhole defect exhibited three stages when immersed in the uncarbonated/carbonated SPS.In the initial stage,steel in defect was passivated when exposed in the uncarbonated SPS and corroded when exposed in the carbonated SPS,due to competitive adsorption between chloride and hydroxyl ions.In the second stage,the oxide film under coating reconstituted (the thickness and defects density decreasing) in the uncarbonated SPS,which was caused by the synergy between high hydroxide and chloride activity,while in the carbonated SPS,crevice corrosion happened under the coating around pinhole,because of the different oxygen concentrations cell at the coating/steel interface.In the third stage,localized corrosion occurred under the coating around the pinhole in the uncarbonated SPS,which was probably induced by ion diffusion at the nano-scale coating/steel interface.The corrosion products adjacent to the defects were re-oxidized from FeCl2·4H2O and Fe2(OH)3Cl to Fe2O3·H2O,and the corrosion area was expanded outward in the carbonated SPS.
其他文献
Three-dimensional parts of the 30CrMnSiA steel were successfully fabricated using selective laser melting (SLM).The microstructures and mechanical properties of the SLM-processed 30CrMnSiA samples were investigated by scanning electron microscope and tran
The crevice corrosion behaviors of 436 stainless steels in chloride-containing solutions with sulfate addition were studied using potentiodynamic,galvanostatic and repassivation potential measurements.The results of these electrochemical tests were compar
The hot deformation behavior and processing map of Cu-bearing 2205 duplex stainless steel (2205-Cu DSS) were investigated at temperatures of 950-1150 ℃ and strain rates of 0.01-10 s-1.The effects of Cu addition and different deformation parameters on defo
In this study,series of nanolayered structures of Zn-Al LDHs were prepared by urea hydrolysis.Nanofibers and nanonets of the Al-doped ZnO were formed via the decomposition of the nanolayers under high pressure and temperature.Nanospheres were also prepare
A356-carbon nanofibers (CNFs) composites with different contents of CNFs were fabricated by ultrasonic vibration casting to investigate the effect of CNFs in the matrix on the mechanical properties and wear resistance.The worn surfaces were investigated u
In this work,the influence of pulse current parameters on springback and bending force of magnesium alloy during electropulse-assisted (EPA) V-bending was investigated.The experimental results showed that pulse current can effectively reduce the springbac
The unique phase transformation and carbide evolution in 9Cr18 steel were investigated during semi-solid forming and subsequent heat treatment.The functional gradient thixoforging 9Cr18 component was divided into inner area and edge area.Microstructure ev
This study examines the relationship among cooling rate,microstructure and mechanical properties of a sand-casted A1-5.0Mg--0.6Mn-0.25Ce (wt％) alloy subjected to T4 heat treatment (430 ℃ × 12 h + natural aging for 5 days),and the tested alloys with wall t
In this study,Al matrix nanocomposites containing 1,2 and 4 wt％ nano-boron nitride were fabricated by mechanical milling and hot extrusion.The mechanical properties of all extruded samples were evaluated.Also,the morphology and microstructure of the mille
The GH4169 superalloy with different content of δ-Ni3Nb phase was welded by tungsten inert gas welding.A detailed study of microstructure and hardness of heat-affected zone (HAZ) was performed in both as-welded and aged state.The results show that the pre