【摘 要】
：
瓷件涂膏后烧结的原工艺为:在炉温1500℃时,将钼舟推入预热区,分三次预热45分钟,推入高温区保温1小时,再推入冷却区,分四次冷却70分钟后取出。约3小时烧1舟。按此工艺,大瓷
论文部分内容阅读
瓷件涂膏后烧结的原工艺为:在炉温1500℃时,将钼舟推入预热区,分三次预热45分钟,推入高温区保温1小时,再推入冷却区,分四次冷却70分钟后取出。约3小时烧1舟。按此工艺,大瓷件因炸裂报废数很大。如Fu-66F/Z上瓷环(95瓷外径φ112,内径φ102,高32)一次金属化后瓷炸率达30～40％。
Porcelain pieces of paste after sintering the original process: At a furnace temperature of 1500 ℃, the molybdenum boat into the preheating zone, three warm-45 minutes, into the high temperature insulation for 1 hour, then pushed into the cooling zone, divided into four After cooling for 70 minutes, remove. About 3 hours to burn a boat. According to this technology, a large number of scrap pieces of large scrap. Such as Fu-66F / Z porcelain ring (95 porcelain outer diameter φ112, inner diameter φ102, high 32) after a metal porcelain fried rate of 30 to 40%.
其他文献
《医药导报》杂志系中国药理学会、华中科技大学同济医学院附属同济医院联合主办的医药专业期刊,国内外公开发行。是国家科技部中国科技论文统计源期刊(中国科技核心期刊),北
载波300路主群信号编码设备要求时钟频率稳定度为±20×10~(-6)。但是,石英谐振器在宽温度(-40～+70℃)范围内的频率相对偏移量为10~(-5)。为了满足钟频稳定度、设备小型化和
砷化镓肖特基势垒场效应晶体管在1微米结构下实现了f_(max)在30千兆赫以上(比已经报导的其它晶体管的f_(nax)高2.5倍)。报导了详细的测量结果同时讨论了已经达到的或者是希望
一、等效磁荷、磁库伦定律 B=H+4πM∵▽,B=O, ∴▽·H=-4π▽·M=4πP_M,(1) 其中 P_M=-▽·M (2)称为磁荷密度。永磁系统的H又满足▽×H=0 (3)
First, the equivalent ma
衡水中学平湖分校又一次引发人们对衡中模式的争论,仍然是众说纷纭、各执一词,还是有那么多似是而非的奇谈怪论,为衡水中学辩护、认为衡水中学被妖魔化的声音也十分响亮,不明
专利的详细说明:本专利是有关将来白天线的超高频、甚高频信号通过一根电缆接到电视输入端的电视显像方式,目的在于不使用分配器即可收到的超高频、甚高频信号分别输入到超
每年一度的微处理器论坛可以称得上是CPU产业的圣殿,只有最顶尖级的人物才能参加;它也是未来一年CPU产业的灯塔,指出未来CPU产业的走向。从CPU产品的发展趋势角度来看,每年1
我在佛山统战部工作多年,分管海外联谊工作,结识不少港澳朋友,其中就有潘以和先生。他个子不高,但很健壮,脸上长带笑容,为人和善,是一位朴实、忠厚,爱国爱乡,备受敬重的人士
她是北京市保安系统第一批网络女保安队员中的一员;她矫弱的身躯里有着男保安的刚毅,又有着女保安的文静;她以突出的工作能力成为分公司首位女保安队长;她在两年多的保安历
一、专业解析管理科学与工程是将自然科学与社会科学相结合、定性方法与定量方法相结合、理论与实际相结合,以管理科学为基础,多学科知识为支撑,利用现代信息技术,解决各领域