【摘 要】
：
经过许多予实验可如在硝酸银—硫代硫酸钠酸性镀液中添加ZV—19添加剂,在一定的电解条件下(PH4.2～4.6,温度10～25℃电流密度0.4～1.6A/dm~2,电镀时间10～15min,机械搅拌),可以获得良
论文部分内容阅读
经过许多予实验可如在硝酸银—硫代硫酸钠酸性镀液中添加ZV—19添加剂,在一定的电解条件下(PH4.2～4.6,温度10～25℃电流密度0.4～1.6A/dm~2,电镀时间10～15min,机械搅拌),可以获得良好的镜面光泽银镀层。认为镀液是由于焦亚硫酸钠的同离子效应而稳定。在镀液中银离子与硫代硫酸根离子反应而主要生成[Ag(S_2O_3)_2]~(3-)络阴离子。本文在开发新的镀银液的同时也研究了电解条件、镀层的性能等。
After many experiments can be as silver nitrate - thiosulfate acid bath add ZV-19 additive, under certain electrolysis conditions (PH4.2 ~ 4.6, temperature 10 ~ 25 ℃ current density of 0.4 ~ 1.6A / dm ~ 2, electroplating time 10 ~ 15min, mechanical stirring), you can get a good mirror silver coating. It is considered that the plating solution is stable due to the same ion effect of sodium metabisulfite. In the bath, silver ions react with thiosulfate ions to form [Ag (S_2O_3) _2] ~ (3-) complex anions. In this paper, the development of new silver plating solution also studied the electrolysis conditions, the performance of the coating.
其他文献
据《中国电子报》2007年11月13日报道,最近,东芝全额出资的加贺东芝电子正式启动了用于功率半导体的该公司首条200 mm晶圆生产线。新生产线面向功率半导体的前工序。东芝的目
随着工业生产的发展,噪声对环境的污染及对人类的危害也日益严重。为了贯彻安全生产和以预防为主的方针,国家卫生部和国家劳动总局于1980年1月颁布了《工业企业噪声卫生标准
台架如图所示。使用时,把手电钻紧固在台架上,装上所需钻头,扳下扳手,即可钻孔。当扳手压力去除后可自动上升复位。如钻盲孔,将深度尺寸定好即可。
As shown in the pictur
挤齿工装(图1)可用在车床上,来挤压工件(图2)两端的三角形花键齿。原工艺是放在卧铣上由形角度铣刀,一齿齿地铣出,两端所需工时50min/件。而采用改进后的工装挤压,3min即可
Nd1.85Ce0.15Cu1-xMnxO4 samples with doping level up to 20% have been synthesized by solid-state reaction method. The influence of Mn on their normal-state trans
1985年9月24日至10月24日我随一汽赴日联合设计代表团去日本洽谈有关一汽变速箱分厂热处理设备联合设计事宜,并对日本三家热处理炉制造厂和十一家渗碳热处理设备使用厂进行
一、1988年回顾 1988年在我国经济生活中出现了一些不稳定因素。这些不稳定因素在生产资料流通领域的主要表现是: (一)主要生产资料供求矛盾进一步加剧 1988年我国主要生产
中型高压异步电动机(H355～500)机座统一为箱式板焊结构。定子铁心为外压装吊入式或压入式。我厂试制的机座为外压装吊入式。这种结构刚性较差,我厂机座加工习惯都是用立车加
众所周知,在酸性冲天炉熔炼过程中,由于焦炭的增硫影响,经熔炼后铸铁的硫含量往往是增大的。在生产球铁件时,原铁水硫含量高,球化难,衰退快,球化所需的残留镁量和残留稀土量
一、对目前流行的消费膨胀概念的看法目前,在对消费问题的研究中,概念用得很乱,有的叫消费膨胀,有的说消费基金膨胀,有的称消费需求膨胀,因此,有必要对这三个流行的名词及其