Preparation of BN/SiO2 ceramics by PIP method

来源 :中南工业大学学报(英文版) | 被引量 : 0次 | 上传用户:roattrjca
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
The precursor infiltration and pyrolysis(PIP) method for preparation of BN/SiO2 composites was used to improve mechanical properties, dielectric properties and feasibility of high temperature dielectric parts with large dimensions and complex shapes. In the processing procedure, the porous BN ceramic matrix was first successfully prepared by compacting the mixed powders of B and BN and then sintering them at a certain temperature under normal pressure of N2.The polycarbosilane(PCS) solution was vacuum infiltrated into porous BN ceramics at the room temperature and then at 800 ℃ in the air to depolimerize out amorphous SiO2, and sintered further at 1 300 ℃ in N2 to get BN/SiO2 composites. The microstructure of materials was studied by means of X-ray diffraction and electron probe micro analysis. The thermo-decomposition mechanism of PCS was investigated by a TG-DTA and infrared (IR) spectrum analysis. The flexural strengths were measured by the three-point bending method. The dielectric constant and the loss tangent were measured by the wave-guide method. The results show BN/SiO2 composites were fabricated. The obtained composites posses a flexural strength of 61.9693.31 MPa, the dielectric constant in the range of 3.503.78 and the order of magnitude of the loss tangent at 10-3, which are good for the high temperature dielectric parts with large size and complex shapes.
其他文献
以健康鲜鸡血为原料,对制备亚硝基血红蛋白的最佳pH值、亚硝酸钠、抗坏血酸的最佳添加量等合成条件进行了研究.结果表明,亚硝酸钠的最佳添加量为0.3g/100mL血液;以抗坏血酸为
Synchronization with lower SNR hadnt been considered by the conventional publications. Based on the Synchronized multi-carrier CDMA plus (SMCC + ) system, which
服装图形设计涉及大量几何计算和图形设计,设计过程高度依赖设计师的经验.鉴于以上特点及CBR具有可直接利用相似实例的解来求解目标问题的特性,因此选用CBR为该智能系统的解
目的 探讨以不同置换液剂量行连续性静脉静脉血液滤过(CVVH)对多器官功能障碍综合征(MODS)疗效的影响.方法 回顾性分析成都军区总医院自2004-01~2010-10期间行CVVH治疗的68例M
To improve the solid lubricity on the worn surface of frictional-pairs, a convenient and simple brushpainting technique was utilized to prepare the solid lubric
The structure and performance of space-time multiuser detection receiver at base stations of WCDMA system is analyzed, in which smart antenna is employed. WCDMA
目的 探讨青海省近10年鼠疫流行势态,为制订预防控制对策提供依据。方法 应用Excel 2003软件统计2001- 2010年青海省地方病预防控制所人间鼠疫病例数据库、鼠疫监测和鼠疫疫源
A novel surface-repairing technique for gun bore was investigated, which was combined with the merits such as anti-erosion wear, damage-repairing, and etc. It w
The availability using oxygen-rich powders to prepare ultrafine Ti(C,N)-based cermets was investigated. The deoxidation process, denitrification phenomenon and
The nonstoichiometric La-rich mischmetal (designated by Ml)-based hydrogen storage alloy with a composition of Ml(Ni0.64Co0.20Mn0.12Al0.04)4.76 was prepared by