Improving wear resistance of magnesium alloy AZ91D by TiN-CrN multilayer coating

来源 :中国有色金属学会会刊(英文版) | 被引量 : 0次 | 上传用户:jn27
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
Applying a novel method of arc-glow plasma depositing, a 2 μm-thick coating with 12 sub-layers of TiN and CrN was deposited alternately on the surface of magnesium alloy AZ91D to improve its wear resistance. The wear behavior was investigated by test of ball on disc sliding. The composition and microstructure of the coating were also analyzed by means of X-ray diffraction (XRD) and glow discharge spectrum (GDS), and the morphology of TiN-CrN film was surveyed through scanning electronic microscopy (SEM) and atom force microscopy (AFM).The adhesion strength between film and matrix was evaluated by ways of stick-peeling test. The surface micro-hardness of the coating is above HK0.011 433, and the specific wear ratio of specimens coated with TiN-CrN films tested decreases greatly compared to that of the bare metal.
其他文献
Solid state B-offerings (FeB compound) were used for plasma-assisted boronizing on Ti6Al4V alloy by double glow discharge plasma alloying technique (DGPSA). Dur
Al2O3(f)/TiAl composites were synthesized by an exothermic reaction method using Ti, Al and TiO2 powders doped with Nb2O5 and La2O3. The effect of Nb2O5 and La2
The effect of heat-treatment process on the properties of Mm0.8Mg0.2(NiCoAlMn)3.5 hydrogen storage alloy was discussed. The electrochemical properties such as c
The effects of Ethylene- Vinyl Acetate copolymer ( EVA ) latex as an additive or a glass fiber sur face modifier on the properties of Glass- Fiber ( GF ) / Magn
The magnetic and structural properties of 2% Ni-doped ZnO powers prepared by sol-gel method were studied. X-ray diffraction (XRD) and high resolution transmissi
The synthesis of nanosized powders and their assembly is of considerable importance to the microelectronics industry because of the pervasive drive to miniaturi
The synthesis of precursor of green phosphors, LaPO4:Ce, Tb, by means of co-precipitation with cocurrent flow feed was studied. The effects of the reaction temp
Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitra
A novel double metal cyanide complex (DMC) based on Zn[Ni(CN)4] was prepared using K2[Ni(CN)4] and ZnCl2, and employed as catalyst for the copolymerization of c
A simple method was presented to produce a micro-droplet of sulphuric acid on a pre-selected micro-zone on a pure iron surface with the tip of an AFM cantilever