论文部分内容阅读
摘要：这些年在借鉴国外的建筑保温技术的基础之上，通过国内的一些研究机构和厂家的努力，相继开发出了聚苯颗粒类、无机复合类保温浆料和聚苯板薄抹灰、聚氨脂喷涂等外墙外保温系统，还有保温砌块、复合保温板等多种保温材料和技术，这些材料及技术的推广与应用，推动我国建筑保温业的快速发展。
关键词：建筑节能 保温 施工技术 质量问题
Abstract: Based on referring the oversea construction heat preservation technology in recent years, and the hardwork by some demestic research organizations and factories, our country has developed polystyrene granules series, inorganic composite heat preservation mortar, the wall external heat preservation series including polystyrene board plasterer, polyurethane plating and so on, and also heat preservation building block, composite heat preservation boatd and some other heated material and technologies. The promotion and application of the mateials and technologies drive the development of construction heat preservation of our countr.
Keywords: building energy conservation; heat preservation; construction technology; quality Issues
中图分类号：TU201.5 文献标识码： A 文章编号：
目前，我国的建筑节能工作己经由北向南推进，先后发布实施了《民用建筑
节能设计标准(采暖居住建筑部分)》、《夏热冬冷地区居住建筑节能设计标准》、《夏热冬暖地区居住建筑节能设计标准》。在施工中由于施工操作原因而产生质量问题的很多，因此，规范外保温工程施工操作，加强施工过程中的严格质量监控，是保证外保温工程质量的重要控制手段。施工中容易出现的主要质量问题归纳为：
一、外保温系统的脱落
1、选择的材料性能达不到要求，采用机械固定时锚固件的有效锚固深度和锚固数量不能满足设计要求;粘结胶浆现场配比不准确;施工过程中粘结面积过小，不能满足粘结强度标准。
2、基层表面的平整度超出基层规范允许偏差范围;其表面含有妨碍粘贴的物质，未进行界面处理。
3、采用的聚苯板密度不足，抗拉强度过低，满足不了保温系统自重及面层荷载对其强度的承载要求，导致聚苯板被拉损破坏。
二、保温板的空鼓、虚贴
1、基层墙面的平整度不达标，墙面过于干燥，墙体接触面不够坚实；雨后墙面含水量过大，墙体表面形成水膜，导致板材粘结的空鼓、虚贴。
2、胶浆的配制稠度过低，粘结剂的粘度指标不合理，胶浆贴附到墙面时产生流挂，导致板面局部空点虚贴。
3、施工时不是用双手均匀的挤、揉、压板面，而是用力猛压板的一端造成另一端翘起，在敲、拍、震动板面时，引起胶浆脱落，导致板面的空鼓、虚贴。
三、冬季内墙面返霜结露
1、保温结点设计方案不完善，形成局部热桥断点。
2、施工时聚苯板的切割尺寸不符合要求，施工质量粗糙造成板間缝隙过大，也没有做相应的板条填塞处理。
四、面层的空鼓、开裂
1、水泥的掺入比例过大，胶浆的强度标号过高，面层胶浆早期收缩过快；胶浆的吸水率过高，冬季因冻融、冻胀作用等均会引起开裂。
2、工程用砂选用中砂，导致砂的过筛粒径过细，含泥量过高，粒径级配不合理造成开裂。在施工现场就地搅拌双组分聚合物砂浆，人工配料，配料不准。
3、聚苯板没有完成对外保温养护期的要求，上墙后产生较大的后收缩，引起面层的开裂;聚苯板粘贴时局部通缝或在窗口四角没有套割引起开裂。
4、胶浆没有进行充分搅拌，保温板板面不平，特别是相邻板面不平，造成抹灰厚度偏差，收缩不一致导致裂缝。
5、窗口周边、四角及墙体转折处等易产生应力集中的部位，如门窗洞口的四角处沿450未设增强网格布以分散其应力;抹底层胶浆时，直接把网格布铺设于墙面上，胶浆与网格布不能很好的复合，网格布起不到约束和分散应力的作用而引起开裂。
6、面层未设保温系统的变形缝而引起开裂;在保温系统的截止部位，对材质变换处的防水处理或柔性、刚性的处理不当，产生裂缝。留设伸缩缝时，缝的宽度超过30mm、小于10mm，缝内未放置聚乙烯棒材等隔离材料、未填嵌密封膏，仅用金属压型板进行简单封闭，或填嵌的密封膏性能不配套或已老化，失去防水密封功能。
7、面层使用钢丝网增强时，采用普通的水泥砂浆，因而导致钢筋、水泥砂浆、聚苯板、冷拔钢丝的膨胀系数不一致从而产生开裂。
8、装饰缝不平直，砂浆等残渣在缝内未清除，使雨水积聚在装饰缝内。
9、外墙饰面砖粘贴时施工不严谨，为求快捷，常常在饰面砖周边抹灰后便进行粘贴，造成饰面砖空鼓不饱满，下雨时形成蓄水空腔。
五、结束语
施工中要对施工人员施工面的质量跟踪，及时发现问题及时解决坚决不能把不合格的成品带入下一个工序，在问题没弄清没解决前不能放手。要配备了解工艺相同专业的管理人员实施技术分析，施工技术交底检查验收，资料整理报备。使外保温施工管理程序化、有效化!
关键词：建筑节能 保温 施工技术 质量问题
Abstract: Based on referring the oversea construction heat preservation technology in recent years, and the hardwork by some demestic research organizations and factories, our country has developed polystyrene granules series, inorganic composite heat preservation mortar, the wall external heat preservation series including polystyrene board plasterer, polyurethane plating and so on, and also heat preservation building block, composite heat preservation boatd and some other heated material and technologies. The promotion and application of the mateials and technologies drive the development of construction heat preservation of our countr.
Keywords: building energy conservation; heat preservation; construction technology; quality Issues
中图分类号：TU201.5 文献标识码： A 文章编号：
目前，我国的建筑节能工作己经由北向南推进，先后发布实施了《民用建筑
节能设计标准(采暖居住建筑部分)》、《夏热冬冷地区居住建筑节能设计标准》、《夏热冬暖地区居住建筑节能设计标准》。在施工中由于施工操作原因而产生质量问题的很多，因此，规范外保温工程施工操作，加强施工过程中的严格质量监控，是保证外保温工程质量的重要控制手段。施工中容易出现的主要质量问题归纳为：
一、外保温系统的脱落
1、选择的材料性能达不到要求，采用机械固定时锚固件的有效锚固深度和锚固数量不能满足设计要求;粘结胶浆现场配比不准确;施工过程中粘结面积过小，不能满足粘结强度标准。
2、基层表面的平整度超出基层规范允许偏差范围;其表面含有妨碍粘贴的物质，未进行界面处理。
3、采用的聚苯板密度不足，抗拉强度过低，满足不了保温系统自重及面层荷载对其强度的承载要求，导致聚苯板被拉损破坏。
二、保温板的空鼓、虚贴
1、基层墙面的平整度不达标，墙面过于干燥，墙体接触面不够坚实；雨后墙面含水量过大，墙体表面形成水膜，导致板材粘结的空鼓、虚贴。
2、胶浆的配制稠度过低，粘结剂的粘度指标不合理，胶浆贴附到墙面时产生流挂，导致板面局部空点虚贴。
3、施工时不是用双手均匀的挤、揉、压板面，而是用力猛压板的一端造成另一端翘起，在敲、拍、震动板面时，引起胶浆脱落，导致板面的空鼓、虚贴。
三、冬季内墙面返霜结露
1、保温结点设计方案不完善，形成局部热桥断点。
2、施工时聚苯板的切割尺寸不符合要求，施工质量粗糙造成板間缝隙过大，也没有做相应的板条填塞处理。
四、面层的空鼓、开裂
1、水泥的掺入比例过大，胶浆的强度标号过高，面层胶浆早期收缩过快；胶浆的吸水率过高，冬季因冻融、冻胀作用等均会引起开裂。
2、工程用砂选用中砂，导致砂的过筛粒径过细，含泥量过高，粒径级配不合理造成开裂。在施工现场就地搅拌双组分聚合物砂浆，人工配料，配料不准。
3、聚苯板没有完成对外保温养护期的要求，上墙后产生较大的后收缩，引起面层的开裂;聚苯板粘贴时局部通缝或在窗口四角没有套割引起开裂。
4、胶浆没有进行充分搅拌，保温板板面不平，特别是相邻板面不平，造成抹灰厚度偏差，收缩不一致导致裂缝。
5、窗口周边、四角及墙体转折处等易产生应力集中的部位，如门窗洞口的四角处沿450未设增强网格布以分散其应力;抹底层胶浆时，直接把网格布铺设于墙面上，胶浆与网格布不能很好的复合，网格布起不到约束和分散应力的作用而引起开裂。
6、面层未设保温系统的变形缝而引起开裂;在保温系统的截止部位，对材质变换处的防水处理或柔性、刚性的处理不当，产生裂缝。留设伸缩缝时，缝的宽度超过30mm、小于10mm，缝内未放置聚乙烯棒材等隔离材料、未填嵌密封膏，仅用金属压型板进行简单封闭，或填嵌的密封膏性能不配套或已老化，失去防水密封功能。
7、面层使用钢丝网增强时，采用普通的水泥砂浆，因而导致钢筋、水泥砂浆、聚苯板、冷拔钢丝的膨胀系数不一致从而产生开裂。
8、装饰缝不平直，砂浆等残渣在缝内未清除，使雨水积聚在装饰缝内。
9、外墙饰面砖粘贴时施工不严谨，为求快捷，常常在饰面砖周边抹灰后便进行粘贴，造成饰面砖空鼓不饱满，下雨时形成蓄水空腔。
五、结束语
施工中要对施工人员施工面的质量跟踪，及时发现问题及时解决坚决不能把不合格的成品带入下一个工序，在问题没弄清没解决前不能放手。要配备了解工艺相同专业的管理人员实施技术分析，施工技术交底检查验收，资料整理报备。使外保温施工管理程序化、有效化!