现代表面电化分析技术已用于各种激活与寿命状态下氧化物阴极的研究。我们所关注的是基金属介面层和涂层表面的成份的变化以及它们与逸出功率变化的关系。没有观察到表面单原子层的存在,并且注意到其电化性能与在Bao单晶薄膜中观察到的现象类似。
Modern surface electrochemistry analysis techniques have been used for the study of oxide cathodes under various activation and lifetime conditions. Our concern is the change in the composition of the metal interface and coating surfaces and their relationship to the change in power escaped. No presence of a surface monatomic layer was observed and it was noticed that the electrochemical performance was similar to that observed in the Bao single crystal film.