Barium ferrite micro/nano fibers were successfully prepared via the electrostatic spinning by using dimethyl formamide (DMF) as the solvent, and poly vinyl pyrrolidone (PVP) as the spinning auxiliaries. Effects of strontium substitution on the structure,
【机 构】
：
Key Laboratory for Liquid-Solid Structural Evolution & Processing of Materials Ministry of Education
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Barium ferrite micro/nano fibers were successfully prepared via the electrostatic spinning by using dimethyl formamide (DMF) as the solvent, and poly vinyl pyrrolidone (PVP) as the spinning auxiliaries. Effects of strontium substitution on the structure, morphology, and magnetic properties were investigated by scanning electron microscope (SEM), X-ray diffraction analysis (XRD), and vibration sample magnetometer (VSM). XRD patterns of the samples confirm that pure barium ferrite fibers form, and the Sr substitution makes the main peaks (110), (107), and (114) move to right slightly. Also, the FE-SEM images show that the Sr substituted fibers can keep complete fibrous morphology. Moreover, the VSM results demonstrate that the saturation magnetization can reach 56.7 emu/g when the fibers are calcined at 800℃.
其他文献
Hydraulic characteristic is a good indication of binder hydration,which determines the strength development of cemented paste backfill (CPB).Therefore,the hydraulic characteristic should be communicated with the mechanical property to provide an advanced
We investigated the influences of process parameters on the head curvature of pure titanium sheet in hot rolling process and proposed the controlling means.First,the thermal simulation experiments for pure titanium TA1 were carried out to investigate the
A new kind of corrosion resistant steel for cargo oil tanks (COT) was developed. The influences of final rolling temperature, cooling rate, and final cooling temperature on microstructure were investigated. The proper rolling process parameters were obtai
Al2O3/SiO2 multilayer high-reflective (HR) mirrors at 355 nm were prepared by electron beam evaporation, and post-irradiated with Ar/O mixture plasma. The surface defect density, reflective spectra, and laser-induced damage characteristics were measured u
In order to prepare hydrophobic waterborne polyurethane coatings with better performances, the silicon-containing waterborne polyurethane (SiWPU) with functional chain extender hydroxyethyl acrylate (HEA) was prepared first, and then a series of silicon&f
Bacillus subtilis was selected as the suitable microorganism,which could produce alkaline phosphatase and constantly hydrolyzed phosphate monoester in the mixture solution of bacteria with substrate,and then the PO 4 3-was obtained.Bio-phosphate cement wa
Zinc oxide nanoparticles were synthesized using bovine serum albumin as stabilizers through a facile one-pot strategy in aqueous media. The morphology and crystal phase of the zinc oxide nanoparticles were determined by transmission electron microscopy, X
The surface reconstructing of vermicular alpha-alumina exposed under electron-beam irradiation was investigated by a scanning electron microscope with 0.5 keV beam energy and by a transmittance electron microscope at room temperature and 90 K, respectivel
Fly ash and diatomite were mixed uniformly and ground within various time scale and fly ash/diatomite admixtures with variable particle sizes were obtained. Effects of particle size distributions of the admixtures on the mechanical properties and porosity
We prepared graphene oxide(GO) saturable absorber (SA) successfully through optical deposition method, which is a simple but effective approach to deposit various materials onto substrate under the effects of light, and investigated several factors that i