【摘 要】
：
In order to develop high-performance diamond wheels, the vitrified bond with different contents of Li2O addition and corresponding diamond composites were prepared. The experimental results show that the addition of a small content of Li2O leads the forma
【机 构】
：
School of Materials Science and Engineering,Wuhan University of Technology,Wuhan 430070,China
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
In order to develop high-performance diamond wheels, the vitrified bond with different contents of Li2O addition and corresponding diamond composites were prepared. The experimental results show that the addition of a small content of Li2O leads the formation of the mullite phase in vitrified bond. When the Li2O content is 3wt％, the mullite content in the vitrified bond reaches the maximum. Whereas, the vitrified bond turns into a pure glass phase when the Li2O content further increases to 5wt％. The softening temperature of vitrified bond, wetting angle between the vitrified bond and the diamond film decrease with the increasing of the Li2O content. The softening point of the vitrified bond with 5wt％ Li2O is 537 ℃ and the contact angle is 32°, which are 44 ℃ and 44° lower than those of the sample without Li2O. The CTE (coefficient of thermal expansion), the flexural strength and hardness of the diamond composite sample first increase and then decrease with the increasing of the Li2O content. When the Li2O addition is 3wt％, the flexural strength and hardness of the composites reaches the maximum values of 93 MPa and 98 HRB, respectively, which are 43.1％ and 12.6％higher than those of the sample without Li2O.
其他文献
Non-spherical colloidal silica nanoparticle was prepared by a simple new method,and its particle size distribution and shape morphology were characterized by dynamic light scattering (DLS) and the Focus Ion Beam (FIB) system.This kind of novel colloidal s
A simulation study was carried out by using dissipative particle dynamics (DPD) method to explore the effects of properties of coating chains,such as length,density,rigidity of polymer chains,as well as the distance between nanoparticles on bonding reacti
The electronic structure and the magnetic properties of Fe2Si bulk have been calculated by the first-principle density function theory method.The band structure shows that the hexagonal Fe2Si bulk is ferromagnetic which is a metal structure under spin-up,
Mullite and corundum co-bonded SiC-based composite ceramics (SiC-mullite-Al2O3) were prepared by using SiC, calcined bauxite and kaolin via pressureless carbon-buried sintering. The low-cost SiC-based composite ceramics designed in this study are expected
TiO2 nanopowders with different nitrogen (N) dopant concentrations were first synthesized by sol-gel method.XRD,TEM,HRTEM,XPS,UV-vis DRS were used to characterize the effects of N doping on the microstructures and optical properties of TiO2.The results in
Influence of structural variations of N-vinylimidazolium tetrahalogenidoferrate (III) magnetic ionic liquids (MILs) on thermal properties was investigated. Using Gaussian09/B3PW91/6-311G (2d, p) density functional methods, the microstructure of the MILs w
To improve both oxygen evolution efficiency and stability at high temperatures,Mn,Mn+Mo,Mn+Mo+V,and Mn+Fe+V oxide electrodes were prepared on a Ti substrate,with an intermediate layer of IrO2,by an anodic deposition method.The crystal structure,surface mo
Different heating treatments with the variation of heating rates, holding temperatures and holding time were used to simulate the LTPS procedure. The experimental results show that the reheating shrinkage rates of glass substrates are rarely changed with
We fabricated the nanofiber composite membranes by impregnating Nafion into the modified polyvinylidene fluoride(PVDF) electrospinning nanofiber mat for proton exchange membrane fuel cells applications. The hydrophobic PVDF nanofibers mat became to the hy
To investigate the acoustic emission (AE) characteristics of quasi-brittle materials like rock and concrete, and to further analyze their damage and failure mechanism under seismic and other dynamic loads, the uniaxial tension test of granite cylinder spe