ZK60B (Mg-6％ Zn-0.6％ Zr) alloy joints fabricated by bobbin tool friction stir welding(BTFSW) with various traverse speeds were investigated.The sound joint fabricated by the BTFSW was possible under the appropriate welding parameters.The severe plastic deformation during BTFSW resulted in dispersion and segregation of the Zr-rich particles within the stirred zone(SZ) followed by evolution of a bimodal grain structure with distributed bands of 0.8-1.7 μm ultra-fine grains and 4.1-7.1 μm equiaxed grains.Micro-hardness of SZ is substantially reduced in con-trast to that of parent metal (PM) in spite of the finer grain size owing to dissolution of Mg-Zn based precipitates having hardening effects on alpha-Mg matrix.With the decrease in traverse speed,randomization degree of the plasticized metal flow increases,which is evidenced by the ran-domized arc line pattern at the low traverse speed.Among all defect-free joints,the 200 mm/min joint exhibits the weakest isotropy of texture within SZ and the best tensile properties,which has reduced ultimate tensile strength and yield strength by 5.4％ and by 22.2％,respectively,as com-pared to the PM.The randomized texture hinders the joint fracturing within SZ at low elongation.Therefore,a relatively high elongation of 10.8％ was achieved,which corresponded to 72％ of the PM value.