【摘 要】
：
采用费氏粒度分别为2.5μm和1.0μm的WC粉和Co粉为原料粉末,以ZrO_2(3Y)、CeO_2为添加剂,制备WC-6%Co硬质合金试样,研究了不同添加剂对WC-6%Co硬质合金组织和性能的影响。结
【机 构】
：
中南大学粉末冶金国家重点实验室,长沙中南凯大粉末冶金有限公司,
论文部分内容阅读
采用费氏粒度分别为2.5μm和1.0μm的WC粉和Co粉为原料粉末,以ZrO_2(3Y)、CeO_2为添加剂,制备WC-6%Co硬质合金试样,研究了不同添加剂对WC-6%Co硬质合金组织和性能的影响。结果表明,ZrO_2(3Y)呈球形弥散分布于粘结相中,提高了硬质合金的抗弯强度,但对WC晶粒度无明显影响;CeO_2能细化WC晶粒,减小硬质合金的孔隙,使硬质合金组织分布均匀,抗弯强度提高。
WC-6% Co cemented carbide samples were prepared by using WC powder and Co powder with Fischer-Tropsch particle size of 2.5μm and 1.0μm respectively and ZrO_2 (3Y) and CeO_2 as additives. The effects of different additives on WC- Effect of 6% Co Carbide Microstructure and Properties. The results show that ZrO_2 (3Y) is spherically dispersed in the binder phase and improves the flexural strength of cemented carbide but has no obvious effect on the grain size of WC. CeO_2 can refine the WC grains and reduce the wear resistance of cemented carbide Of the pores, so that the distribution of cemented carbide, bending strength increased.
其他文献
采用萃取法回收氨制取氯化铵工艺替代传统的中和蒸发结晶工艺。通过有机相的选型和应用,对APT产品蒸发结晶工序回收的稀氨水进行萃取回收,采用浓盐酸反萃制取氯化铵并将其返回流程配制解吸剂。整个过程在相对密闭系统中进行,减少了氨气的泄漏,改善了工作环境。
本文是司马相如年谱，《史记·司马相如列传》：“司马相如者，蜀郡成都人也，字长卿。少时好读书，学击剑，故其亲名之曰犬子。”《子虚之赋》为相如在梁时所作，据“居数岁”暂系于本年。
“彤管”一词，首见于《诗经·邶风·静女》，原诗如下：“静女其姝，俟我于城隅。爱而不见，搔首踟蹰。静女其娈，贻我彤管。 彤管有炜，说怿女美。自牧归荑，洵美且异。匪女之为美，美人之
关于边让，《后汉书·文苑传》有传。但传中全载其《章华台赋》和蔡邕《荐举边让书》，对其生平事迹，仅粗述五大阶段履历：少辩博；能属文，作《章华台赋》；为大将军何进征召，署为令史，并为
《僮约》，西汉王褒撰。《汉书·王褒传》曰：“王褒字子渊，蜀人也。”宣帝时曾为谏大夫。萧统《文选》录王褒作品三篇：《洞箫赋》(卷十七)、《圣主得贤臣颂》(卷四十七)、《四子讲
谢庄(421—466)字希逸，陈郡阳夏人，是南朝刘宋一代的著名作家，也是东晋南朝谢氏文学集团中的重要成员之一。谢庄的高祖谢万，是东晋名相谢安之弟。曾祖谢韶，官至车骑司马。本文介绍
从降低生产成本的角度考虑,尝试在真空炉中采用一步烧结法制备梯度结构硬质合金。实验研究了烧结工艺参数对合金显微结构及密度的影响,结果表明:梯度结构硬质合金样品表层的W
上海古籍出版社出版由曹林娣、李泉辑注的古代笑话专集《启颜录》，面世已有15年了，此书《前言》称：“本书汇集历代《启颜录》旧辑本进行辑录，按版本时代先后序次。据以辑录的本子
自唐穆宗长庆四年(825)韩愈弟子李汉编定《昌黎先生文集》40卷(合目录共41卷)，到北宋欧阳修时，250余年间，《韩集》40卷的规模基本无大的变化。其间经晚唐五代的战乱和北宋立国之
国秀集》作为“唐人选唐诗”之一种，其编选者是唐天宝时的进士芮挺章，值得注意的是，芮挺章为何要编选《国秀集》?他的编选原由是什么?这是一个值得思考的问题。但就目前所能见到