Radiofrequent magnetron sputtering technique was used to produce calcium phosphate coated on the titanium substrates, and the sputtered coating films were crystallized in an autoclave at 110 ℃ using a low temperature hydrothermal technique. The crystallization of as- sputtered coating film on the titanium substrates were amorphous calcium phosphate film. However, after the hydrothermal technique, calcium phosphate crystals grew and these were columnar crystal. The Ca/ P ratio of sputtered coating films in 1.6 to 2.0.