焊接接头的多次返修试验

来源 :焊接 | 被引量 : 0次 | 上传用户:qhp168
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
在焊接过程中,常常由于焊工技术不熟练或因工作疏忽大意等,致使焊接接头出现各种不允许存在的缺陷,如成形不良,气孔、夹渣,未焊透等。为了消除这些缺陷使焊件达到技术条件的要求,必须将焊缝缺陷铲除从新焊补(即返修)。这种情况在我厂常有发生,特别是机车锅炉焊缝,经x光检查发现的内部缺陷,由于铲除时缺乏准确性或因第二次焊接时又产生了缺陷,有的焊缝铲焊竟达两三 In the welding process, often due to unskilled welder technology or negligence due to negligence, resulting in a variety of imperfections in the welded joints, such as poor forming, porosity, slag inclusion, incomplete penetration and so on. In order to eliminate these defects so that the weldment to meet the technical requirements, the weld defects must be removed from the new welding repair (that is, rework). This situation often occurs in our plant, especially locomotive boiler welds, the internal defects found by X-ray examination, the lack of accuracy due to eradication or because of the second welding has a defect, and some weld shovel welding As many as two or three
其他文献
以测量物理和力学性能变化的方法,研究不同冷拔变形度对阿尔德莱依型铝合金时效过程中固溶体分解各階段的影响。结果指出冷拔变形显著加速时效过程的进行,并由计算出的α固溶
我厂在车制锁接头(如图1)等零件的内螺纹孔时,采用了一种不停车装卸活的夹具,经使用证明:它不但能保证工件内孔与外圆的同心度,并且能显著地节约辅助时间和提高生产效率。现
我国目前的社会救助制度强调底线公平,政府在其中的主要职能体现为收入再分配,即进行收入转移,保证贫富差距在一个合理的范围内。而社会救助应该涉及对起点公平、过程公平和
最近我们利用车间的废物配制成了一种铸钢件的冒口发热剂。经过试用证实效果良好,现将试用情况介绍如下:1.发热剂的成份:熔化铝合金和铝切削时的炉渣40%,煅件的氧化铁皮45%,
民族自治地方司法机关相对于民族自治地方的立法、行政机关而言具有特殊性,它不是民族自治地方的自治机关,不享有自治权,民族自治地方司法机关相对于非民族自治地方的司法机
SNAI 在线——上海国家会计学院远程教育网(www.esnai.net)是财政部重点建设的会计和财务管理人员远程教育网站,是财政部指定全国会计专业技术资格考试辅导网站。2004年与中
4月10日,索尼公司与三星电子公司签订了第八代非晶TFT液晶显示面板的意向书,双方各投入10亿美元在韩国建立第八代非晶TFT液晶面板生产线。双方最终协议将在6月底之前签订,明
A.床身结构 曲柄压床的床身是金属最多的部件。床身重量约为整个机器重量的60%。同时,床身又是最复杂的和制造时劳动量最大的部件;一般,它受到压床所发出来的基本力量。这样
我厂热处理车间中温箱型电炉的炉底纲板,是用镍铬耐热钢,在使用过程中经常发生断裂变形现象,需要翻换新的炉底钢板。但这种钢板市场很难买到,为了解决这问题,我厂试制一种高
现在,在我国的机械制造业中已广泛地应用了高频 电流感应加热淬火,但是高频电流发生装置的效能并没有充分的被利用。在苏联,由于在高频电流感应加热淬火中广泛地应用了导磁体