【摘 要】
:
Based on the heat transfer theory and liquid solidification theory, the heat transfer during the rapid solidification process of amorphous ribbons prepared by m
【机 构】
:
State Key Laboratory of Powder Metallurgy
论文部分内容阅读
Based on the heat transfer theory and liquid solidification theory, the heat transfer during the rapid solidification process of amorphous ribbons prepared by melt spinning was approximately modeled by one-dimensional heat conduction equation. Besides, integration with the temperature gradient, the relationship between the ribbon thickness and solidification time was derived according to the boundary conditions of ribbon-copper wheel. A simply theoretical model was obtained to calculate the cooling rates of aluminum amorphous ribbons. According to the above theoretical model, the critical cooling rate of aluminum amorphous ribbons by melt spinning is above 106 K/s, which proves that the aluminum based alloys belong to the marginal glass forming ability of alloys. The calculated results are in good agreement with other estimated values reported previously.
其他文献
Depositing silver on magnesium alloy by both electroless plating and organic coatings was studied. The organic coating was made by immersing samples in organosi
The refining and modification effect of Ti (from GRAI), B, Sr and RE (cerium-riched mixtures of rare earth) on the mechanical properties of A356 aluminum alloys
TiC-TiB2-Cu composites were produced by self-propagating high-temperature synthesis combined with pseudo hot isostatic pressing using Ti, B4C and Cu powders. Th
The superplastic forming potential of two fine-grained 5083 aluminum alloys were studied under biaxial tension using a pneumatic bulge test. Experiments were pe
The influences of preparation conditions of Al-5Ti-B (as-cast and hot-rolled) and Al-10Sr (as-cast and hotextruded) and melt treatment procedures on the grain r
A model considering quantitative effects of diffused carbon and nitrogen gradients and kinetics of phase transformation is presented to examine metallo-thermo-m
The microstructural evolution of cold-rolled aluminum alloy 3003 during annealing was investigated by means of micro-hardness measurement, electrical resistivit
A series of new microwave dielectric ceramics Ba3-nLa1+nTinNb3-nO12 (n=0,1,2) were prepared in the BaO-La2O3-TiO2-Nb2O5 system by high temperature solid-state r
The microstructures of the AZ91D die-cast magnesium alloy were investigated by scanning electron microscopy (SEM), X-ray diffractometry (XRD) and energy dispers