植物油基醇酸树脂的制备及其性能研究

来源 :热固性树脂 | 被引量 : 0次 | 上传用户:koel
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
以大豆油和丙三醇为主要原料,氢氧化锂为催化剂,利用醇解反应得到大豆油多元醇,并将其作为二元醇引入到典型的醇酸树脂合成配方中,部分取代丙二醇与顺丁烯二酸酐和邻苯二甲酸酐合成醇酸树脂,再用苯乙烯对合成的树脂进行改性.利用红外光谱仪和同步热分析仪等分析方法研究了合成的醇酸树脂的综合性能.实验表明,醇酸树脂的最佳制备条件如下:油度40%,顺丁烯二酸酐和苯乙烯的质量分数分别为5%、33%,反应温度190~200℃,反应时间3h,得到的醇酸树脂干燥速度最快,固体质量分数为68%,粘度为250 mPa·s,热稳定性较好,涂层力学性能最好.“,”Using soybean oil and glycerol as the main raw materials and lithium hydroxide as catalyst,the soybean oil polyol was obtained by the alcoholysis reaction and introduced into a typical alkyd resin synthesis formular.As a diol,partially replacing the propylene glycol,the soybean oil polyol was reacted with maleic anhydride and phthalic anhydride and the alkyd resin was synthesized.Then the synthesized resin was modified with styrene.The comprehensive performance of the synthesized alkyd resin was studied by using infrared spectrometer and synchronous thermal analyzer.The results showed that the drying speed of the alkyd resin was the fastest as the preparation conditions as follows:oil length 40%,maleic anhydride amount 5%,styrene amount 33%,reaction temperature 190-200 ℃ and reaction time 3 h.The solid content was 68 % and the viscosity was 250 mPa·s.The stability of the resin was good and the mechanical properties of the coatings were the best.
其他文献
以不同地区人工林红松(Pinus koraiensis)母树结实量为研究对象,对球果数量相同的红松母树其单个球果种子质量的差异性进行分析.研究结果显示:单株所结球果数量相同的红松母
为了解民勤荒漠区野生黑果枸杞(L ycium ruthenicum Murr.)种群空间分布特征,阐明环境因素对其的影响程度,本研究采用点格局分析方法,对不同土壤类型、不同龄级黑果枸杞种群
以聚硫橡胶、乙二胺为原料合成了新的环氧树脂固化剂(简称DAJL),通过力学性能测试研究了其用量对环氧固化产物性能的影响。结果表明,随着DAJL用量的增加,环氧树脂固化物的拉