15% Ag-added cubic perovskites Sr0.9La0.1TiO3 and Ruddlesden-Popper(RP) phases Sr2.7La0.3Ti2O7 were fabricated via hydrothermal synthesis,cold pressing and high-temperature sintering.The structure and thermoelectric properties were also investigated for all samples.The results indicated that Ag precipitated as a second phase.Ag addition made electrical conductivity and absolute Seebeck coefficient enhanced,as a result,the ZT values were enhanced both for two series.Compared with cubic perovskite,RP phase was subjected to smaller impact by Ag addition.The reasons for enhancing ZT value and the different impact for two series by Ag addition were also discussed.
15% Ag-added cubic perovskites Sr0.9La0.1TiO3 and Ruddlesden-Popper (RP) phases Sr2.7La0.3Ti2O7 were fabricated via hydrothermal synthesis, cold pressing and high-temperature sintering. The structure and thermoelectric properties were also investigated for all samples The results indicated that Ag precipitated as a second phase. Ag addition made electrical conductivity and absolute Seebeck coefficient enhanced, as a result, the ZT values were enhanced both for two series. Compared with cubic perovskite, RP phase was subjected to smaller impact by Ag addition. Reasons for enhancing ZT value and the different impact for two series by Ag addition were also discussed.