【摘 要】
：
研究了螯合电磷光聚合物PFBtpIrm的光致发光、电化学和电致发光特性,并通过优化器件结构提高聚合物的电致发光性能.发现在聚合物中加入PBD使发光效率降低;而加入PVK空穴传输
【机 构】
：
浙江大学现代光学仪器国家重点实验室,华南理工大学高分子光电材料与器件研究所,浙江大学现代光学仪器国家重点实验室,浙江大学现代光学仪器国家重点实验室,浙江大学现代光学仪器国家重点实验室 杭州310024
论文部分内容阅读
研究了螯合电磷光聚合物PFBtpIrm的光致发光、电化学和电致发光特性,并通过优化器件结构提高聚合物的电致发光性能.发现在聚合物中加入PBD使发光效率降低;而加入PVK空穴传输层后,由于能量有效地转移到电磷光聚合物中,器件性能提高.基于器件ITO/PEDOT/PVK/PFBtpIrm5/Ba/Al,在电流密度为10.0mA/cm2时,最大外量子效率为4.25%,饱和红光的色坐标为(0.69,0.29).
The photoluminescence, electrochemical and electroluminescent properties of the chelating phosphorescent polymer PFBtpIrm were studied, and the electroluminescent properties of the polymer were optimized by optimizing the device structure. It was found that adding PBD to the polymer decreased the luminescent efficiency, PVK hole transport layer, the device performance is improved due to the energy transfer into the electro-phosphorescent polymer.Based on the device ITO / PEDOT / PVK / PFBtpIrm5 / Ba / Al, the maximum external quantum at the current density of 10.0mA / cm2 The efficiency is 4.25%, the color coordinate of saturated red light is (0.69,0.29).
其他文献
研究了催化反应Flickering振子在多频率确定性谐和外力和有界随机噪声联合作用下,系统安全盆的侵蚀和混沌现象.将Melnikov方法推广到包含有限多个频率外力和随机噪声联合作用
采用甘氨酸.硝酸盐(GNP)法合成了中温固体氧化物燃料电池阴极材料Ba0.4Sr0.6Co1-xFexO3-δ=0.0～0.8)系列粉体.利用XRD和SEM对材料的结构和微观形貌进行分析,用直流四端子法测
教师在进行小学语文的课堂教学过程中，应当将学生作为教学的主体，充分让学生发挥自身的主体作用，充分激发学生的学习兴趣，充分调动学生的积极性。课堂气氛的活跃能够极大地提升课
针对折叠结构萨尼亚克(Sagnac)光纤传感阵列存在噪声光与信号光混叠的问题,提出了一种主动相位偏置时分复用方案。在传统梯形结构传感阵列的基础上,通过调整总线光纤的长度关
设计并合成了9种未见文献报道的N-(5-邻氯苯基-2-呋喃甲酰氨基硫羰基)-L-α-氨基酸乙酯衍生物,其结构经IR,1HNMR,MS和元素分析测试确证.MTT法测试结果表明大部分目标化合物对
介绍利用20 GW加速器二极管产生的电子束源,开展s波段相对论速凋管振荡器(RKO)的理论设计、粒子模拟和实验研究的情况.该RKO采用3个紧密耦合的圆柱腔作为振荡腔,束流经过一段
数值研究了各向异性光反馈注入的垂直表面发射激光器(VCSEL)的矢量偏振模转换机理,研究结果表明,首先,当注入电流接近阈值电流时,由VCSEL的外部参数和偏振器控制的光反馈注入
建立了一维半导体Ge激光烧蚀模型,对不同功率密度的紫外激光烧蚀半导体Ge的过程进行了模拟,并对计算结果进行了分析,得到激光功率密度对烧蚀过程以及蒸气膨胀动力学特性的影
提出了一种利用双池受激布里渊散射(SBS)系统选用混合介质,进而测量SBS介质布里渊线宽的方法.在紧凑双池SBS系统的放大池中放入待测介质,在振荡池中放入布里渊频移可调的混合
采用三维时域有限差分算法(3D-FDTD)对GaAs/AlGaAs量子阱红外探测器(QWIP)的顶部光子晶体光输入耦合层结构的电磁场分布进行了仿真分析,得到了多种不同周期、占空比、深度的