【摘 要】
：
Zn2SnO4/few-layer boron nitride nanosheets (FBNNS) hybrids were synthesized via a one-step hydrothermal method. The structures, morphology, optical properties, electron transformation and separation of the as-prepared products were characterized by X-ray
【机 构】
：
School of Materials Science and Engineering, Hebei Provincial Key Laboratory of Traffic Engineering
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Zn2SnO4/few-layer boron nitride nanosheets (FBNNS) hybrids were synthesized via a one-step hydrothermal method. The structures, morphology, optical properties, electron transformation and separation of the as-prepared products were characterized by X-ray diffraction, transmission electrical microscopy, UV-vis diffuse reflectance spectroscopy and electrochemical impedance spectroscopy, respectively. Rhodamine B was used to evaluate the photocatalytic activities of the as-prepared samples under visible light illumination. The photocatalytic mechanism was also explored. Experimental results showed that the degradation efficiency of rhodamine B was firstly increased and then decreased with increasing the usage amount of FBNNS. When it was 9 wt％ based on the weight of Zn2SnO4, the degradation efficiency of the as-prepared Zn2SnO4/FBNNS-9 wt％composites reached to the maximum of 97.5 ％ in 180 min, which was higher than 39.2 ％ of pure Zn2SnO4. Moreover, the holes played mainly active roles in photocatalytic reaction process. In addition, the as-prepared hybrids could enhance the separation efficiency of photoexcited carriers compared to pure Zn2SnO4.
其他文献
A diamond-like carbon (DLC) film was deposited on YT14 substrate using magnetron sputtering (MS). The surface morphologies, roughness and bonding spectra of obtained film were characterized using scanning electron microscopy (SEM), atomic force microscopy
The effects of circulating fluid bed (CFB) ash on the adsorption performance of polycarboxylate superplas-ticiser and the mechanism of this influence on the dispersive property of the polycarboxylate superplasticiser were investigated by determing the cem
The semisolid A356 alloy strip was prepared by a novel continuous micro fused-casting process. The microstructure evolution and mechanical property of A356 aluminum alloy strip with different nozzle temperatures were investigated. The nozzle temperature h
The water absorption and desorption processes of different types of lightweight aggregates were studied. Subsequently, the influences of pre-wetting lightweight aggregates on compressive strength, microhardness, phase composition, hydration parameters and
The effects of Cr3+,Cu2+,and Pb2+ on compressive strength,reaction products,and pore structures of fly ash based geopolymer were studied.In addition,the immobilization and bonding interaction between heavy metal and fly ash based geopolymers were investig
Plasma-enhanced CVD (PECVD) epitaxy at 200 oC was used to deposit heavy doped n-type silicon films. Post-annealing by rapid thermal processing was applied to improve the properties of the epitaxial layer. By analyzing the Raman spectra and the imaginary p
In order to investigate how to enhance the teeth fracture resistance after the post and core treatment, an in vitro study was conducted to measure the fracture resistance of endodontically treated teeth restored with cast post and core with two kinds of s
The effect of spherical particle size on the surface morphology, electrochemical property and processability of lithium iron phosphate was systematically studied. Spherical lithium iron phosphate with different particle size distributions controlled with
A modified co-precipitation method for the production of Cu/ZnO/Al2O3 complex was studied. The modification was that part of Al was introduced by adding Al3+ into Cu2+/Zn2+ solution, and the rest of Al was added after co-precipitation step in the form of
A new method of fabricating C/C composite materials, namely electric heating CVD method, was used, which electrified the carbon fiber directly by using the conductivity of itself. Acetylene was used as the carbon source with nitrogen as dilution gas, and