【摘 要】
：
采用动态硫化法制备NR/EPDM/POE热塑性弹性体来增容NR/EPDM共混胶,通过改变增容剂的含量研究NR/EPDM共混胶的力学性能、微观形态性能、耐热性能。结果表明,随着弹性体增容剂
【机 构】
：
青岛科技大学橡塑材料与工程教育部重点实验室,
论文部分内容阅读
采用动态硫化法制备NR/EPDM/POE热塑性弹性体来增容NR/EPDM共混胶,通过改变增容剂的含量研究NR/EPDM共混胶的力学性能、微观形态性能、耐热性能。结果表明,随着弹性体增容剂的增加,NR/EPDM共混胶的拉伸性能、撕裂性能、硬度都有上升趋势,拉断伸长率无明显变化;在NR/EPDM中添加20份弹性体增容剂,可以达到较高的力学性能和耐热空气、耐臭氧老化性能。
The NR / EPDM / POE thermoplastic elastomer was prepared by dynamic vulcanization to compatibilize NR / EPDM blend rubber. The mechanical properties, microstructure and heat resistance of NR / EPDM blend rubber were studied by changing the content of compatibilizer. The results show that with the increase of elastomer compatibilizer, the tensile properties, tear properties and hardness of NR / EPDM blend tend to increase, while the elongation at break has no obvious change. In NR / EPDM, 20 Part of the elastomer compatibilizer, can achieve higher mechanical properties and heat-resistant air, ozone aging resistance.
其他文献
诱发电位是反映中枢神经系统功能的指标之一，应用电生理监测脊髓功能的实验和临床研究逐渐开展。本文介绍了采用电生理方法，探索脊髓慢性损伤后中枢神经诱发电位的改变，实验过程
目的：初步建立大鼠颈神经背根节(DRG)压迫模型，系统观察压迫损伤后DRG神经元病理学改变。方法：选用3月龄SPF级SD雄性大鼠20只，随机分为假手术组和压迫组，采用自制硅胶片压迫左侧C6
研究了原位生成甲基丙烯酸钠(NaMAA)和DCP对NR/BR/TPI并用胶性能的影响。结果表明,当DCP用量一定时,随着NaMAA理论生成量的增加,拉伸强度和撕裂强度先增加后减小,硬度、定伸
目的：研究正常和抗-Fas抗体诱导凋亡大鼠纤维环细胞的基因表达谱，分析抗-Fas抗体诱导凋亡大鼠纤维环细胞基因表达水平的变化。方法：建立大鼠颈椎间盘纤维环细胞培养体系，使用抗-F
广东省最近提出15条支持房企应对房市变化的意见。对在2008年签订土地出让合同、确实无法按时缴纳土地出让价款的项目用地,由土地使用者申请并经当地市、县人民政府批准,可适
以两步法工艺合成聚氨酯弹性体,通过改变多元醇、异氰酸酯种类以及扩链剂种类及配比等,考察了原料种类对聚氨酯弹性体力学性能及耐水性能的影响。结果表明,多元醇种类、异氰
目的：观察益气化瘀利水方对实验性骨关节炎兔软骨中转化生长因子-β1的影响。方法：按Colombo法建立家兔膝骨关节炎模型，将20只新西兰大白兔随机分为正常组、模型组、中药组(益气
以镀银铝粉为高导电填料,硅橡胶为基材,对胶料性能和硫化体系、偶联剂用量进行了研究。结果表明,当镀银铝粉用量为260份,硫化体系选用DBPMH,偶联剂选用A151,硫化条件为160℃
据中国化工和石油网消息,墨西哥一研究机构发现垃圾中的常见真菌可以分解那些原本认为很难再循环利用的聚氨酯污染物。据项目组负责人称,研究团队不仅明确了最佳分解真菌,而且还能将催化分解的关键酶进行隔离。这些微生物可以分解50%以上的床垫泡棉,其中20%的分解效果明显高于世界各地实验
探讨益气化瘀方及拆方对椎间盘软骨细胞凋亡状态下Bax、Bcl-2及Caspase8表达的调控情况。抗Fas抗体诱导养大鼠椎间盘软骨细胞凋亡，通过益气化瘀方及拆方益气方、化瘀方药理血