【摘 要】
：
A series of Y2Ti2O7 microwave dielectric ceramics were synthesized by conventional solid-state method.The effects of rare earth oxide (La2O3,CeO2,Nd2O3,Sm2O3,Eu
【机 构】
：
College of Materials Science and Engineering,Jiangsu Provincial Key Laboratory of New Materials of I
论文部分内容阅读
A series of Y2Ti2O7 microwave dielectric ceramics were synthesized by conventional solid-state method.The effects of rare earth oxide (La2O3,CeO2,Nd2O3,Sm2O3,Eu2O3,Gd2O3 and Dy2O3) and Nd2O3 doping content on the microstructure and dielectric properties of Y2Ti2O7 ceramics were investigated.The experimental results showed that the rare earth ions were considered to dissolve in Y-sites of the pyrochlore structure,different rare earth oxides and concentration had different influences on Y2Ti2O7 ceramics.It was found that the rare earth oxide could decrease dielectric loss obviously,and the τf could be adjusted to zero with proper concentration.The Y2Ti2O7 ceramics with 1 mol.% neodymium oxide(Nd2O3) added showed optimum comprehensive properties,with the sintering temperature 1450 ℃,the permittivity 45,the value of Q·f22000 GHz,and the τfvalue 179 ppm/℃,while 1 mol.% Nd oxide (Nd2O3) was added.
其他文献
Ti4+-mixed FePO4·xH2O precursor was prepared by co-precipitation method, with which Ti4+ cations were added in the process of preparing FePO4·xH2O to pursue a
A cerium-triethanolamine complex was obtained by the reaction of cerium(Ⅲ) nitrate and triethanolamine in ethanol solution.Spontaneous oxidation of cerium(Ⅲ)
The structural and electronic properties of bulk and (001) plane of TiC were investigated by the first-principles total-energy pseudopotential method based on d
Mechanical activation was used to improve the extraction of chromium in molten NaOH. It is observed that the extraction ratio reaches 97% after leaching for 200
High temperature tensile properties and microstructure evolutions of twin-roll-cast AZ31B magnesium alloy were investigated over a strain rate range from 10-3 t
The recent results on hydrothermal synthesis of mixed rare earth-alkali or ammonium fluorides were presented.The initial ratios of the starting materials,pH val
The brazing of 55% SiCp/A356 (volume fraction) composites in air using Zn-Al alloy as a filler metal was investigated. During the brazing process, ultrasonic vi
Microstructure,tensile properties and compressive creep behaviors of Mg-(1.65-11.52) wt.% Sn-2 wt.% Nd alloys were studied in this paper.The microstructure of t
Stoichiometric and amorphous Er2O3 films were deposited on Si(001) substrates by radio frequency magnetron technique.Spectroscopic ellipsometry measurement show