Balancing the strength and ductility of Mg-6Zn-0.2Ca alloy via sub-rapid solidification combined wit

来源 :材料科学技术:英文版 | 被引量 : 0次 | 上传用户:zhangyong131420
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
In this study,we successfully prepared a Mg-6Zn-0.2Ca alloy by utilizing sub-rapid solidification(SRS)combined with hard-plate rolling(HPR),whose elongation-to-failure increases from~17%to~23%without sacrificing tensile strength(~290 MPa)compared with its
其他文献
The phase equilibria and thermodynamic properties of the U-Nb system were investigated through experiments and thermodynamic modeling.In the experiments,a serie
Marine biofouling is a major issue deteriorating the service performance and lifespan of marine infrastruc-tures.The development of a durable,long-term,and envi
This work aims at understanding the features of the Sn grains from which whiskers preferentially grow.The growth behavior of Sn whiskers on a 50 μm thick hyper
In recent years,the Ti2AlNb-based alloys are selected as potential alloys for elevated temperature appli-cations to replace conventional Ni-based superalloys ow
Public safety incidents caused by bacterial infections have attracted widespread attention towards antibacterial textiles (fibers,fabrics,etc.).Nevertheless,it
So far,only two orientation relationships(OR)between hexagonal close-packed(HCP)(αphase)and facecentered cubic(FCC)structures in zirconium and titanium alloys have been reported.Here a new type FCC phase(named γ phase)with OR:<11■0>α‖<
本文针对2×660 MW机组锅炉送风机在正常运行过程中出现由叶片断裂造成的设备运行参数异常,进行原因分析,并结合断裂原因总结本次送风机叶片断裂事故的教训,从而为后续或同类型风机设备的检修提供参考依据。
Laser powder bed fusion (L-PBF) was utilized to produce specimens in Ti-6Al-4V,which were subjected to a bi-lamellar heat treatment,which produces microstructur
In this work,the beneficial effect of Sn addition on the corrosion resistance mechanism of Cr-Mo low alloy steel was studied.Results demonstrated that Sn improves the corrosion resistance of the steel matrix mainly by influencing the microstructural trans
The highly thermal stability precipitates strengthen creep resistance for alloys,which require precipitates to resist coarsen at elevated temperature.In the Mg-