【摘 要】
：
In Nb-Si based alloys with a two-phase NbSS/ intermetallic Nb5Si3 structure, the Nb5Si3 provides high-temperature strength, while the Nb solid-solution phase, N
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
In Nb-Si based alloys with a two-phase NbSS/ intermetallic Nb5Si3 structure, the Nb5Si3 provides high-temperature strength, while the Nb solid-solution phase, NbSS, contributes to room-temperature ductility and toughness. The results show that in Nb-15W-10Hf-xSi alloys (x = 0.5, 5 and 18, mole fraction, %), the volume fraction of the Nb5Si3 is 0 for the 0.5% Si sample, 15% for the 5% Si sample and the 50% for 18% Si sample. With increasing Si content, i.e., the Nb5Si3 fraction, the high-temperature strength is improved considerably, but room-temperature ductility and toughness are degraded. For the sample Nb-15W-10Hf-18Si with 50% Nb5Si3, the compressive strength at 1 500 ℃ and the room-temperature fracture toughness are 500 MPa and 6.8 MPa-m1/2, respectively, those for the Nb5Si3 free sample, Nb-15W-10Hf-0.5Si, are 190 MPa and 13.6 MPa-m1/2.
其他文献
Several tensile samples were prepared using laser rapid forming (LRF) with Ti-6Al-4V alloy as powder material, and the samples were annealed. The microstructure
Cermet composites containing mixture of noble metal phase and electrolyte phase are the state-of-the-art electrode materials used for electrochemical sensor and
Lead zirconate titanate (PZT)/polyvinylidenc fluoride (PVDF) 0- 3 piezoelectric composites doped with polyaniline (PANI) were obtained by hot-press method.The p
The brittleness generation mechanism of high strength lightweight aggregate concrete(HSLWAC) was presented, and it was indicated that lightweight aggregate was
In this paper, any two of the three anticorrosion agents, that is emulsifier (OP-10), soluble glass (Na2O·nSiO2) and glycerin (C3H8O3), were treated simultaneo
By indentation at room temperature followed by annealing at high temperatures, the pinning effect of germanium on dislocations in germanium-doped Czochralski si
The static and dynamic magnetic controlling characteristics of NiMnGa magnetically controlled shape memory alloy (MSMA) were experimentally studied. The results
The hollow sphere fly ash/6061Al composite with about 43% porosity in volume fraction (produced by the addition of hollow sphere fly ash particles) was fabricat
ZnFe2O4-based inert anodes were made to conduct the aluminum electrolysis tests. The corrosion behaviors of the inert anodes were examined and discussed. Experi
A 2D woven graphite fibers reinforced aluminum matrix composite with 50%Grf (volume fraction) was fabricated by the squeeze-casting technology, and its microstr