Through hydrothermal process, the chrysanthemum-like ZnO particles are prepared with zinc acetate dihydrate (Zn(CH3COO)2·2H2O) and sodium hydroxide (NaOH) used as main resources under the different concentrations of surfactant polyacrylamide (PAM). The microstructure, morphology and the electromagnetic properties of the as-prepared products are characterized by high-resolution transmission electron microscopy (HRTEM), field emission environment scanning electron microscope (FEESEM) and microwave vector network analyzer, respectively. The experimental results indicate that the as-prepared products are ZnO single crystalline with hexagona wurtzite structure, that the values of slenderness ratio Ld are different in different PAM concentrations, and that the good magnetic loss property is found in the ZnO products, and the average magnetic loss tangent tan δu increases with PAM concentration increasing, while the dielectric loss tangent tan δe decreases.
The microstructure, morphology of morphology of ruthenium-doped ZnO particles are prepared with zinc acetate dihydrate (Zn (CH3COO) 2 · 2H2O) and sodium hydroxide (NaOH) used as main resources under the different concentrations of surfactant polyacrylamide and the electromagnetic properties of the as-prepared products are characterized by high-resolution transmission electron microscopy (HRTEM), field emission environment scanning electron microscope (FEESEM) and microwave vector network analyzer, respectively. The experimental results that that the as-prepared products are ZnO single crystalline with hexagona wurtzite structure, that the values of slenderness ratio Ld are different in different PAM concentrations, and that the good magnetic loss property is found in the ZnO products, and the average magnetic loss tangent tan δu increases with PAM concentration increasing , while the dielectric loss tangent tan δe decreases.