In this research,the effects of centrifugal radius and mould rotation speed on microstructure in centrifugal-cast Al-Cu alloy have been investigated.The results show that,with increase of the centrifugal radius or mould rotation speed,the grain size of centrifugal-cast Al-Cu alloy decreases gradually,while the content of white phases containing the Al2Cu precipitated from α-phase,divorced eutectic and regular eutectic microstructure increases,leading to higher Cu macrosegregation.The variation level of microstructure in centrifugal-cast Al-Cu alloy at 600 rpm of mould rotation speed is greater than that at 300 rpm.
In this research, the effects of centrifugal radius and mold rotation speed on microstructure in centrifugal-cast Al-Cu alloy have been investigated. With results of show that with increase of the centrifugal radius or mold rotation speed, the grain size of centrifugal-cast Al-Cu alloy minimizes, while the content of white phases containing the Al2Cu precipitated from α-phase, divorced eutectic and regular eutectic microstructure increases, leading to higher Cu macrosegregation. The variation level of microstructure in centrifugal-cast Al-Cu alloy at 600 rpm of mold rotation speed is greater than that at 300 rpm.